SABIC Innovative Plastics NORYL HS2000X PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL HS2000X PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. 17% Mineral reinforced. Non-brominated, non-chlorinated FR system. UL94 V0 and 5VA listing. UL746C f1. Radiant panel listing. Dielectric strength. Dimensional stability. Suitable for E/E market indoor/outdoor applications including electrical ceiling boxes and smoke detectors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.6 g/10 min @Load 5.00 kg, Temperature 280 °C |
7.6 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| 7.6 g/10 min @Load 5.00 kg, Temperature 300 °C |
7.6 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 | |
| Melt Index of Compound | 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 6.0 g/10 min @Load 5.00 kg, Temperature 300 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | ISO 527 |
| 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 71.0 MPa | 10300 psi | ISO 527 |
| 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 8.4 % | 8.4 % | Type I, 5 mm/min; ASTM D638 |
| 10.5 % | 10.5 % | ISO 527 | |
| Elongation at Yield | 3.7 % | 3.7 % | ISO 527 |
| 3.8 % | 3.8 % | ASTM D638 | |
| Tensile Modulus | 3.65 GPa | 529 ksi | 5 mm/min; ASTM D638 |
| 4.00 GPa | 580 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 117 MPa | 17000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 117 MPa | 17000 psi | ISO 178 | |
| Flexural Yield Strength | 117 MPa | 17000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.55 GPa | 515 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 3.67 GPa | 532 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 3.80 GPa | 551 ksi | ISO 178 | |
| Izod Impact, Notched | 1.31 J/cm | 2.45 ft-lb/in | ASTM D256 |
| 8.11 J/cm @Thickness 3.20 mm |
15.2 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Izod Impact, Unnotched | 22.3 J/cm | 41.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/2C |
| Dart Drop, Total Energy | 443 J @Temperature 23.0 °C |
327 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 77.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C | 259 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 117 °C @Thickness 3.20 mm |
243 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 128 °C @Thickness 6.40 mm |
262 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 111 °C | 232 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 116 °C @Thickness 6.40 mm |
241 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 132 °C | 270 °F | Rate B/50; ISO 306 |
| 136 °C | 277 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 100 °C | 212 °F | UL 746B |
| UL RTI, Mechanical with Impact | 85.0 °C | 185 °F | UL 746B |
| UL RTI, Mechanical without Impact | 100 °C | 212 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
UL 94 |
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.20e+16 ohm-cm | 1.20e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 2.89 @Frequency 50.0 - 60.0 Hz |
2.89 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 17.3 kV/mm @Thickness 3.20 mm |
439 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0044 @Frequency 1.00e+6 Hz |
0.0044 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.017 @Frequency 50.0 - 60.0 Hz |
0.017 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 30 - 60 arcs | 30 - 60 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Radiant Panel Listing | YES | UL Tested |
| UV-light, water exposure/immersion | F1 | UL 746C |
Users viewing this material also viewed the following:
- Proto3000 Objet Digital Materials™ DM_8320 Rigid Opaque Prototyping Polymer
- Ineos ABS Centrex® 833 ASA+AES Blend (discontinued **)
- Heatbath/Park Thermo-Quench Quenching and Tempering Salt
- Sylvin Technologies 9077-75 Natural PVC for Injection Molding
- ExxonMobil Mobil Aero HFA
- A. Schulman SCHULAMID® 66 MV3H Unreinforced Nylon 6/6
- Cytec Conathane® CC-1155-35 (Conap) Polyurethane Two-component Dielectric Conformal Coating
- 3M Hi-Strength 94 ET Spray Adhesive-Low VOC
- Caplinq LINQSTAT™ VCF-41014B
- A. Schulman POLYBATCH™ Orange LL10257/4 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved