LATI Laticonther 62 CPG/500 PA 6, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer LATI
Trade Name Laticonther
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laticonther 62 CPG/500 PA 6, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High thermal conductivity product based on Polyamide 6 (PA6). Special filler. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.91 g/cc
0.0690 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0060 cm/cm
0.0035 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0045 - 0.0070 cm/cm
0.0045 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
Elongation at Break 2.0 %
2.0 %
Tensile Modulus 8.50 GPa
1230 ksi
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Thermal Properties Metric English Comments
Thermal Conductivity 1.20 W/m-K
8.33 BTU-in/hr-ft²-°F
Longitudinal
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
Vicat Softening Point 205 °C

@Load 5.00 kg
401 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa