SABIC Innovative Plastics LNP LUBRICOMP 5CL23 FP-V (PVDF)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP 5CL23 FP-V (PVDF).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* 5CL23 is a compound based on PVDF resin containing 15% Carbon Fiber, 10% PTFE. Added features include: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.84 g/cc | 1.84 g/cc | ASTM D792 |
| Density | 1.84 g/cc | 0.0665 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 |
| 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.70 % | 0.70 % | 5 mm/min; ISO 527 |
| 0.80 % | 0.80 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 14.46 GPa | 2097 ksi | 1 mm/min; ISO 527 |
| 15.78 GPa | 2289 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Yield Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.87 GPa | 1722 ksi | 2 mm/min; ISO 178 |
| 12.5 GPa | 1810 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.550 J/cm | 1.03 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.01 J/cm | 3.77 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.52 | 0.52 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.44 | 0.44 | ASTM D3702 Modified |
| K (wear) Factor | 8.06 x 10-8 mm³/N-M | 4.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 331 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 168 °C @Thickness 3.20 mm |
334 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 164 °C @Thickness 3.20 mm |
327 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8512F (842G0) (UF) Synthetic Oil
- Plastcom SLOVAMID 66 OB PA66, optically brightened
- SABIC Innovative Plastics Lexan® FL3000 PC
- Solvay Specialty Polymers Ryton® R-7-120NA Polyphenylene Sulfide Compound (Unverified Data**)
- Teknor Apex Sinvicomp SRP 5602 Polyvinyl Chloride, Rigid
- A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene
- A. Schulman POLYFORT™ FPP 1220 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
- Dow ATTANE™ 4201 Ultra Low Density Polyethylene, Blown Film Grade
- 3M Scotchcal™ 1000-54 Graphic Film
Copyright © lookpolymers.com All Rights Reserved