Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS High heat PC/ABS blend offering high modulus / low CTE and good practical impact |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS (Asia Pacific) High heat PC/ABS blend offering high modulus / low CTE and good practical impact |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® DMX1435 PC Copolymer Lexan* DMX1435 is a UV stabilized standard flow polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® DMX1435 PC Copolymer (Europe-Africa-Middle East) This product will be phased out per January 2015 -- Lexan* DMX1435 is a UV stabilized standard flow polycarbonate copolymer resin with improved scratch resistance. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® DMX2415 PC Lexan* DMX2415 is a polycarbonate resin with improved scratch resistance. Lexan* DMX2415 is available in transparent, translucent, and opaque colors.This data was supplied by SABIC-IP for the Americ.. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® DMX3415 PC Copolymer Lexan* DMX3415 is a co-polycarbonate resin with improved scratch resistance, high purity and optical quality.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® DMX3415M PC Copolymer (Europe-Africa-Middle East) Lexan* DMX3415M is a co-polycarbonate resin with improved scratch and abrasion resistance compared to standard polycarbonate. Lexan* DMX3415M is available in transparent colors. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® DMX9455 PC Copolymer (Europe-Africa-Middle East) Lexan* DMX9455 is a standard flow, flame retardant, V0/1.5mm, opaque polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea.. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer Lexan* DMX9455A is a standard flow, flame retardant, transparent polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | ASTM D790 |
PolyOne Geon™ CPVC MC250 Polyvinyl Chloride, Chlorinated (CPVC) The Geon MC250 CPVC is an injection molding fittings compound for Industrial Pipe applications where enhanced resistance at elevated temperatures is needed. It is listed under NSF Std 14 and 61. Geo.. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® ML7677 PC (Asia Pacific) Transparent Polycarbonate in limited colors. Excellent processability, super high flow, flame retardant, UL rated V-1 at 2.0mm |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer (Asia Pacific) This product will be phased out per January 2015 -- Lexan* DMX9455A is a standard flow, flame retardant, transparent polycarbonate copolymer resin with improved scratch resistance. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP 5CL23 FP-V (PVDF) LNP* LUBRICOMP* 5CL23 is a compound based on PVDF resin containing 15% Carbon Fiber, 10% PTFE. Added features include: Wear Resistant. |
|||
Flexural Yield Strength | 108 - 150 MPa | 15700 - 21800 psi | Average value: 128 MPa Grade Count:5 |
Overview of materials for Ethylene Vinyl Alcohol (EVOH) This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Alcohol". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | Bending Strength; ASTM D790 |
EVALCA EVAL® LC-H101BD Ethylene Vinyl Alcohol Copolymer Resin
(discontinued **) 38 mol % Ethylene.Data provided by EVALCA. Applications: Blown film. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a part of th.. |
|||
Flexural Yield Strength | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
LG Chemical LUMID GP1200A(W) PA6, Medium Viscosity Feature: Injection Molding, PA6, Medium ViscosityApplication: Industrial Material, Sport PartsCAS No. 25038-54-4Information provided by LG Chemical |
|||
Flexural Yield Strength | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP3150A(W) PA6+MF15%, General Purpose Feature: Injection Molding, PA6+MF15%, General PurposeApplication: E&E (Rice Cooer Housing)CAS No. 25038-54-4 and 14807-96-6Information provided by LG Chemical |
|||
Flexural Yield Strength | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY GP5106F PC/ABS+GF10%, Flame Retardance Description: Injection Molding, PC/ABS+GF10%, Flame RetardanceApplication: IT/OA (Housing)CAS: 103598-77-2, 9003-56-9, 68928-70-1, 1309-64-4 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical 82TR SAN, High Transparency, Heat Resistance, Chemical Resistance Feature: Injection Molding, SAN, High Transparency, Heat Resistance, Chemical ResistanceApplication: Refrigerator Sleeves, MiscellaneousCAS No. 9003-54-7Information provided by LG Chemical |
|||
Flexural Yield Strength | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY GN5151RF PC/ABS Mineral Filler Description: Injection Molding, PC/ABS Mineral Filler, General Purpose, High Stiffness, Halogen Free Flame RetardantApplication: E&E (Housing), IT/OA (Notebook PC Housing)CAS: 103598-77-2, 9003-56-9.. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp ZWM2411 PPE+PS (Asia Pacific) Modified PPO*, 30% mineral filled product, V-1@1.5mm, HDT 125degC, low warpage product, BK color onlyThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp ZF0041XC PPE+PS (Europe-Africa-Middle East) LNP* THERMOCOMP* ZF0041XC is a compound based on PPE+PS Blend resin containing Glass Fiber and Flame retardant. Added features include Flame Retardant.This data was supplied by SABIC-IP for the Euro.. |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL GTX GTX675 PPE+PA6 Noryl GTX* GTX675 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to a.. |
|||
Flexural Yield Strength | 108 MPa | 15600 psi | ASTM D790 |
PlastxWorld CEVIAN® S1210 PC/ABS alloy Glass fiber reinforced PC/ABS alloy.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Flexural Yield Strength | 108 MPa | 15600 psi | ASTM D790 |
PlastxWorld CEVIAN®-N 050 SAN resin These are typical values and are not intended for specification purposes. UL approved file No. is E47773.Information provided by PlastxWorld Inc. |
|||
Flexural Yield Strength | 108 MPa | 15600 psi | ASTM D790 |
Cheng Yu Plastic PP237G2 Polypropylene, 20% Glass Fiber |
|||
Flexural Yield Strength | 108 MPa | 15700 psi | ASTM D790 |
Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, Dry As Molded Neat resin, for film or extrusion.Information provided by Cresset Powers Ltd. |
|||
Flexural Yield Strength | 108 MPa | 15600 psi | ASTM D790 |
Cheng Yu Plastic A700UV ABS-UV Resistance |
|||
Flexural Yield Strength | 108 MPa @Thickness 6.40 mm |
15600 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Santron IMS 2007LF SAN Resin High Rigidity Clear SANInformation provided by Bhansali |