- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 158 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 158 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Unannealed; ISO 75-2/A |
| PolyOne OnForce™ LFT PP-60LGF/001 Natural Polypropylene Homopolymer (PP Homopolymer) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP KONDUIT ITF2B PA 6/12 (Asia Pacific) LNP* Konduit* ITF2B is a compound based on Nylon 6/12 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP 5CL23 FP-V (PVDF) LNP* LUBRICOMP* 5CL23 is a compound based on PVDF resin containing 15% Carbon Fiber, 10% PTFE. Added features include: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 - 225 °C | 316 - 437 °F | Average value: 186 °C Grade Count:10 |
| Overview of materials for Phenolic, Resole, Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Resole, Wood Filled". Each property range of values reported is minimum and maximum values of .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP KFL23LH Acetal Copolymer LNP LUBRICOMP* KFL23LH is a compound based on Acetal Copolymer resin containing 15% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Low Extractable. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C @Thickness 3.20 mm |
316 °F @Thickness 0.126 in |
ASTM D648 |
| SABIC Innovative Plastics SABIC STAMAX 30YM240 PP SABIC® STAMAX 30YM240 is a 30% long glass fiber reinforced polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 16496906... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C @Thickness 3.20 mm |
316 °F @Thickness 0.126 in |
ASTM D648 |
| SABIC Innovative Plastics SABIC STAMAX 30YM243 PP SABIC® STAMAX 30YM243 is a 30% long glass fiber reinforced UV stabilized polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMD.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics ULTEM 1285 PEI (Europe-Africa-Middle East) Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact compliant in recognized colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP 4X08423 FP-P (PFA) LNP* THERMOCOMP* 4X08423 is a compound based on PFA resin containing Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP SF004S PA12 LNP* Thermocomp* SF004S is a compound based on Nylon 12 containing 20% glass fiber. Added features include: Heat Stabilized, Healthcare |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP VERTON MV006S PP LNP* VERTON* MV006S is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this material include: Chemically Coupled, Structural. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP VERTON MV006S PP (Asia Pacific) LNP VERTON* MV006S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP VERTON MV006SU PP LNP VERTON* MV006SU is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized, Structur.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C @Thickness 3.20 mm |
316 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL IGN320 PPE+PS 20% glass reinforced PPE + PS. High heat, high modulus automotive applications like ignition coils. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Ultem ATX102R PEI+PCE 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Ultem ATX102R PEI+PCE (Europe-Africa-Middle East) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ASTM D648 |
| Plenco 7523 Phenolic, Granular, Transfer Molded PLENCO 07523 is a woodflour and cotton flock filled novolac phenolic molding compound, formulated for high impact industrial uses. UL recognized under component file E40654.Information supplied by P.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ISO 75-1/-2 |
| Covestro Apec® 1803 Polycarbonate UV-stabilizedsoftening temperature (VST/B 120)=184 °CPreprocessingMax. Water content |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ISO 75-1/-2 |
| Covestro Apec® 1895 Polycarbonate Easy flowingeasy to demoldsoftening temperature (VST/B 120)=183 °CPreprocessingMax. Water content |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Starflam PX06010 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam PX06010 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ASTM D648 |
| Diamond Polymers NYLON 6650HSL Black Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ISO 75/2a |
| Azdel Plus R401B02N 40% Continuous Random Fiber Mat / PP Resin Matrix AZDEL® R401B02N is a random oriented needled continuous glass fiber mat material. This polypropylene composite material features high properties and a basic homogeneous fiber distribution. This m.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | |
| Adell ZR-37 33% Glass Reinforced Nylon/Olefin Alloy Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C @Thickness 3.20 mm |
316 °F @Thickness 0.126 in |
ASTM D648 |
| SABIC Innovative Plastics SABIC STAMAX 40YM243 PP SABIC® STAMAX 40YM243 is a 40% long glass fiber reinforced UV stabilized polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS .. |
|||