- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 168 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 168 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
| NYCOA 1417 HS Heat Stabilized, Impact Modified Nylon 6 Resin NYCOA 1417 HS is a heat stabilized and impact modified Nylon 6. This medium viscosity resin was developed for injection molding and extrusion processes for applications requiring improved toughness,.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
| Nylene® 603 Nylon 6, Extrusion Grade Dry as molded. Extrusion grade. Nylene 603 is a plasticized, high residual monomer resin designed for extrusion applications requiring excellent flexibility, high strength and good abrasion resist.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N2000STHL Nylon 6 (DAM) Information provided by Ravago. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N2000STL Nylon 6 (DAM) Information provided by Ravago. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | ASTM D648 |
| Polymer Resources NY6-IM1 Nylon 6, Impact Modified Nylon 6, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | ASTM D648 |
| Polymer Resources NY6-IM1-[color]-H Nylon 6, Impact Modified, Heat Stabilized Nylon 6, Impact Modified, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grad.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | ASTM D648 |
| Polymer Resources NY6-IM1-[color]H Nylon, Impact Modified, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C @Thickness 3.20 mm |
334 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP 5CL23 FP-V (PVDF) LNP* LUBRICOMP* 5CL23 is a compound based on PVDF resin containing 15% Carbon Fiber, 10% PTFE. Added features include: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
| PolyOne Stat-Tech™ NJ-10SS/000 Nylon 12 - 10% Stainless Steel Reinforced
(discontinued **) Data provided by PolyOne. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Unannealed |
| Aardvark Polymers AARTEL® 2100UV Acetal Homopolymer Rotational Molding Resin Aartel 2100UV is a natural acetal homopolymer with UV stabilizers.Aartel 2100UV is a medium viscosity resin with excellent flow characteristics.Aartel 2100UV is available in natural white and may be.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C @Thickness 3.20 mm |
334 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp RP0049 PA 66 LNP LUBRICOMP* RP0049 is a compound based on Nylon 66 resin containing Flame Retardant, PTFE, Silicone. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP f.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® POM CO GF10 TL10 BK 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightAdditive: PTFE Lubricant(10%)Features: Lubricated, Copolymer, Good Wear Resistance and Low FrictionApp.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PA6/ABS 1120 GF15 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Impact ModifierFeatures: Impact ModifiedAppearance: Natural ColorInformation p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Asia Pacific) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Europe-Africa-Middle East) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics NORYL PPX ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
| Cheng Yu Plastic T881 Flame Retardant PBT |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
| E-Polymers TEKASTER® F101FR Un-Reinforced Flame Retardant PBT Polyester Resin: TEKASTER is thermoplastic polyester resins (PBT, PET) mostly injection molding. PBT has excellent mechanical properties and well balanced engineering plastics with an electrical pe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
| Ensinger Tecaform™ HPV 13 Acetal Homopolymer - Extruded Products (POM) Tecaform™ HPV 13 is a brown homopolymer acetal with an internal PTFE lubricant. Its low coefficient of friction, excellent PV values, toughness, wear resistance, and machinability make it an excep.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM Test |
| BASF Ultramid® 8253 HS PA6 (Dry) Ultramid 8253 HS is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM Test |
| BASF Ultramid® 8253 PA6 (Dry) Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/o.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | |
| Arkema Group Rilsan® BESN G9 TL Nylon 11, Graphite Filled (Conditioned) Designation ISO 1874-PA11,EHLS,18-010,CD10Grade with graphite filler for tubes extrusion. Available color: steel gray. Light and heat stabilized.No need of lubricant. Low friction coefficient. Good .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
| Ashley Polymers Ashlene® RH190ST Acetal A high impact homopolymer resin.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 125 Polypropylene, Glass Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.50% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM Data |
| BASF Capron® 8253 Impact Modified Nylon 6 (Dry)
(discontinued **) Capron 8253 is an unfilled type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Capron 8253 HS) and/or pigmented versions.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® PA 1409 Conductive Thermoplastic Compound PRE-ELEC® PA 1409 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PA 1.. |
|||