- Polymer Property : Tensile Strength at Break = 12200 psi
Polymer Property : Tensile Strength at Break = 12200 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 84.0 MPa | <= 12200 psi | ISO/R527 |
| Polykemi AB POLYfill PPH GF8030 PD1 VT2 PP, Glass Fiber-Reinforced, Chemically Coupled Heat Stabilized Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP 5CL23 FP-V (PVDF) LNP* LUBRICOMP* 5CL23 is a compound based on PVDF resin containing 15% Carbon Fiber, 10% PTFE. Added features include: Wear Resistant. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP KFL25 Acetal Copolymer LNP LUBRICOMP* KFL25 is a compound based on Acetal Copolymer resin containing 25% Glass Fiber, 10% PTFE. Added feature of this material is: Wear Resistant. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer (Asia Pacific) LNP* Lubricomp* KFL36 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp OX95338 PPS (Asia Pacific) LNP* Lubricomp* OX95338 is a compound based on Polyphenylene Sulfide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.Thi.. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 LNP* LUBRICOMP* RN001S is a compound based on Nylon 66 resin containing 2% MOS2. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 (Asia Pacific) LNP* Lubricomp* RN001S is a compound based on Nylon 66 resin containing MOS2. Added features of this material include: Internally Lubricated, Heat Stabilized. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Ultem HFATX200 PEI+PCE High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Europe-Africa-Middle East) High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Xenoy® 1760E PBT+PC 11% Glass Reinforced alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. High flow version of Xenoy 1760 resin. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP 5C004 PVDF (Asia Pacific) LNP* Thermocomp* 5C004 is a compound based on Polyvinylidene Fluoride resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP DF002ERH PC LNP THERMOCOMP* DF002ERH is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Healthcare, Mold Release. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP DX06408 PC LNP THERMOCOMP* DX06408 is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP KF002 Acetal Copolymer LNP THERMOCOMP* KF002 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP KX97390 Acetal Copolymer LNP THERMOCOMP* KX97390 is a compound based on Acetal Copolymer resin containing Glass Fiber. Added features of this material include: Chemically Coupled. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp OF004AER PPS LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SA.. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Thermocomp P1000P PA 6 (Asia Pacific) LNP* Thermocomp* P1000P is a compound based on Nylon 6 resin. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP XFL21R PA LNP* LUBRICOMP* XFL21R is a compound based on Amorphous Nylon resin containing 5% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Mold Release. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP DF002ER PC LNP THERMOCOMP* DF002ER is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding. Mold Release |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Thermocomp P1000P PA 6 LNP* Thermocomp* P1000P is a compound based on Nylon 6 resin. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS LNP* THERMOCOMP* ZF0049 is a compound based on PPE+PS resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Thermotuf VFM53 PA 66 LNP THERMOTUF* VFM53 is a compound based on Nylon resin containing Glass Fiber, Mineral. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas.. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL GFN1410V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1410V resin is a blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 10 % glass reinforcement. The resin is suitable for injection molding. Noryl GFN1410V resin has.. |
|||
| Tensile Strength at Break | 84.1 MPa | 12200 psi | ASTM D638 |
| PlastxWorld CEVIAN® CGF20 20% GF PC/Acrylic Alloy Glass fiber reinforced PC/Acrylic alloy.These are typical values and are not intended for specification purposes. Information provided by PlastxWorld Inc. |
|||
| Tensile Strength at Break | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON KX97157 Acetal Copolymer (Europe-Africa-Middle East) LNP* STATKON* KX97157 is a compound based on Acetal resin containing Carbon. Added features include : Electrically Conductive, Impact Modified. |
|||