SABIC Innovative Plastics Cycoloy® CY5005 PC+ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CY5005 PC+ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applications including business equipment, TV enclosures, among othersThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D 792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.050 %
0.050 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.10 %

@Temperature 23.0 °C
0.10 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 27 g/10 min

@Load 2.16 kg,
Temperature 260 °C
27 g/10 min

@Load 4.76 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
31 g/10 min

@Load 2.16 kg,
Temperature 260 °C
31 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 43.0 MPa
6240 psi
50 mm/min; ISO 527
48.0 MPa
6960 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 63.0 MPa
9140 psi
50 mm/min; ISO 527
65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 34 %
34 %
Type I, 50 mm/min; ASTM D 638
40 %
40 %
50 mm/min; ISO 527
Elongation at Yield 3.5 %
3.5 %
50 mm/min; ISO 527
3.9 %
3.9 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.67 GPa
387 ksi
1 mm/min; ISO 527
2.80 GPa
406 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
97.0 MPa
14100 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.63 GPa
381 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.70 GPa
392 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.690 J/cm

@Temperature -30.0 °C
1.29 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
0.900 J/cm

@Temperature 23.0 °C
1.69 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
10.0 kJ/m²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 20.0 J

@Temperature 23.0 °C
14.8 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 73.0 °C
163 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
81.0 °C

@Thickness 6.40 mm
178 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Vicat Softening Point 89.0 °C
192 °F
Rate B/50; ISO 306
92.0 °C
198 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 2.00 mm
V-0

@Thickness 0.0787 in
UL 94 by SABIC-IP