Resinlab® EP1190 Flame Retardant Epoxy Casting Resin

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Resinlab®
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Resinlab® EP1190 Flame Retardant Epoxy Casting Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resinlab™ EP1190 is a medium viscosity, flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Laboratories Inc., (File# E186034, Project 00NK02738) for UL Standard 94. EP1190 qualifies for a vertical burn rating of V-0 at 6mm thickness. It also gives very good resistance to water, salt spray, inorganic acids and bases and most organic solvents. It cures quickly at room temperature to a tough, semi-rigid polymer. It has good wetting and adhesion to most surfaces and is free flowing to penetrate voids and give good air release. EP1190 was formulated to a 4/1 volume mix ratio for ease of use in automatic mixing equipment with static mixers. It contains soft, low-abrasion fillers which can separate over time, although they have good resistance to hard settling. If used in side-by-side cartridge format, they should be stored at 5C, rotating stock on a FIFO basis. EP1190 will generally reach handle cure at room temperature within 1 to 4 hours depending upon mass and ambient temperature. Full cure usually achieved within 24 – 48 hours. Cure time can be accelerated by the application of heat after product has gelled. Times and temperatures from 2 hours at 60°C to 30 minutes at 100°C are typical for most castings (less than 100 grams).Information Provided by Resinlab L.L.C., an Ellsworth Adhesives Company.
Physical Properties Metric English Comments
Specific Gravity 0.969 g/cc
0.969 g/cc
Part B; TM R050-16
1.50 g/cc
1.50 g/cc
Mixed; TM R050-16
1.68 g/cc
1.68 g/cc
Part A; TM R050-16
Water Absorption 0.17 %

@Time 86400 sec
0.17 %

@Time 24.0 hour
TM R050-35
Viscosity 400 cP
400 cP
Part B, RVT, #3, 20 rpm; TM R050-12
16000 cP
16000 cP
Mixed; TM R050-12
20000 cP
20000 cP
Part A, RVT, #7, 20 rpm; TM R050-12
Mechanical Properties Metric English Comments
Hardness, Shore D 80
80
TM R050-17
Tensile Strength at Break 27.6 MPa
4000 psi
TM R050-36
Tensile Strength, Ultimate 27.6 MPa
4000 psi
TM R050-36
Tensile Strength, Yield 12.4 MPa
1800 psi
TM R050-36
Elongation at Break 0.00 - 1.0 %
0.00 - 1.0 %
TM R050-36
Tensile Modulus 4.48 GPa
650 ksi
TM R050-36
Compressive Yield Strength 51.7 MPa
7500 psi
TM R050-38
Compressive Strength 68.9 MPa
10000 psi
Break; TM R050-38
82.7 MPa
12000 psi
Ultimate; TM R050-38
Compressive Modulus 3.45 GPa
500 ksi
TM R050-38
Adhesive Bond Strength 17.2 MPa
2500 psi
Lap shear; 2024 T3 Al Abraded / MEK Wipe; TM R050-37
Thermal Properties Metric English Comments
CTE, linear 40.0 µm/m-°C
22.2 µin/in-°F
Thermal Conductivity 0.500 W/m-K
3.47 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 150 °C
302 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Glass Transition Temp, Tg 45.0 °C
113 °F
TM R050-25
Electrical Properties Metric English Comments
Volume Resistivity 8.10e+15 ohm-cm
8.10e+15 ohm-cm
Dielectric Constant 4.8

@Frequency 100 Hz,
Temperature 25.0 °C
4.8

@Frequency 100 Hz,
Temperature 77.0 °F
Dielectric Strength 16.1 kV/mm
410 kV/in
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 60.0 °C
2.00 hour

@Temperature 140 °F
1440 - 2880 min

@Temperature 25.0 °C
24.0 - 48.0 hour

@Temperature 77.0 °F
Pot Life 45 min
45 min
Mass: 200g; TM R050-19
Descriptive Properties Value Comments
Color Black
Mix Ratio 4:1
Volume
6.5:1
Weight