Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | Average value: 34.4 MPa Grade Count:11 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "ABS + Glass Blend". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
Tensile Strength, Ultimate | >= 27.6 MPa | >= 4000 psi | Reinforced |
Natural Rubber, Not Vulcanized (NR, IR, Polyisoprene) Natural rubber is polyisoprene. Chemical and environmental resistance and mechanical properties are improved through crosslinking (vulcanizing), usually through treatment with sulfur.Natural rubber.. |
|||
Tensile Strength, Ultimate | >= 27.6 MPa | >= 4000 psi | ISO 1184-1983E |
LyondellBasell Montell 8340 Polybutene-1 Key Features: semi-crystalline low ethylene content random copolymer, miscible with polypropylenes, FDA acceptableApplications: minor additive in a polyethylene peel seal layerMeets FDA requirements.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | 2 in/min.; ASTM D638 |
Ineos K44-06-122 HDPE HDPE K44-06-122 is a natural high density polyethylene copolymer designed specifically for extrusion of potable water, industrial, and mining pipe. It is recognized by the Plastic Pipe Institute as .. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | Machine direction |
Spartech Royalstatâ„¢ R671 ABS Static Control Sheet Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | |
Williams Advanced Alloys WS314A Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D412/D638 |
Lubrizol Estane® MVT 80AF3 Thermoplastic Polyurethane, Moisture Vapor Transmission Type: Estane® MVT 80AF3 TPU is a aromatic polyether-based thermoplastic polyurethane (TPU).Features: High moisture vapor transmission, good low temperature properties and elasticity.Uses: Blown and.. |
|||
Tensile Strength, Ultimate | 27.6 MPa @Temperature 927 °C |
4000 psi @Temperature 1700 °F |
|
Crucible Steel 430 Chromium Steel Crucible 430 is essentially a non-hardenable chromium steel which is adaptable for general purpose corrosion and heat resisting applications. It is prone to slight hardening by heat treatment. This.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM Data |
Dow Prevail® 3100 ABS + Polyurethane PREVAIL® 3100 thermoplastic resin offers designers and manufacturers a combination of flexibility and low temperature toughness not previously available in an engineering thermoplastic and is used .. |
|||
Tensile Strength, Ultimate | 27.6 MPa @Temperature 982 °C |
4000 psi @Temperature 1800 °F |
Transverse |
AK Steel NITRONIC® 19-D Duplex Stainless Steel AK Steel NITRONIC® 19D is a stainless steel with a mixed ferrite and austenite structure. This alloy provides high yield strength (65 ksi minimum {448 MPa}),
good drawing and welding characteristi.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | |
Bulk Molding Compounds BMC 100 Thermoset Polyester, GP BMC 100 is a high strength, low shrink general purpose molding compound. It can be supplied in bulk or extruded in pre-weighted slugs. Due to the excellent flow and controlled reactivity, BMC 100 is.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | |
Bulk Molding Compounds BMC 501E Mineral Filled, Glass Reinforced Polyester BMC 501E molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression and transfer molding. It is a product with good overall electrical properties, flame.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | |
Bulk Molding Compounds BMC 5436 Mineral Filled, Glass Reinforced Polyester BMC 5436 molding compound is a low cost, mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is characterized by good molda.. |
|||
Tensile Strength, Ultimate | 27.6 - 48.3 MPa | 4000 - 7000 psi | |
Bulk Molding Compounds BMC 605LWR Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 605LWR is a mineral filled, glass fiber reinforced polyester bulk molding compound suitable for compression, transfer and stuffer injection molding. It is designed to provide improved wear resis.. |
|||
Tensile Strength, Ultimate | 27.6 - 34.5 MPa | 4000 - 5000 psi | |
Bulk Molding Compounds BMC SLC 1000 Glass Reinforced Polyester BMC SLC 1000 is a medium strength, low-cost, glass reinforced polyester compound with adjustable shrinkage. It is V-0 flame arc and track resistant. UL® recognized. This material was formerly known.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Buckeye Polymers BP RPP 2006 T Polypropylene, 20% Mineral Filled This Talc-filled product exhibits excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and mar resistance, and resis.. |
|||
Tensile Strength, Ultimate | 27.6 - 48.3 MPa | 4000 - 7000 psi | |
Bulk Molding Compounds BMC 1100 Corelyn Glass Fiber Reinforced Polyester Compound BMC 1100, also known as CoreLyn, is a food contact safe material with excellent scratch and stain resistant properties. CoreLyn can be pigmented to match virtually any color. This glass fiber-reinfo.. |
|||
Tensile Strength, Ultimate | 27.6 - 34.5 MPa | 4000 - 5000 psi | |
Bulk Molding Compounds BMC 1410 Electrical Grade BMC 1410 is a high-strength electrical grade material with excellent flammability resistance. In most applications, this material is competitive with SMC. Equal performance at a lower cost. Normally.. |
|||
Tensile Strength, Ultimate | 27.6 - 55.2 MPa | 4000 - 8000 psi | |
Bulk Molding Compounds BMC 324 Automotive Grade Molding Compound BMC 324 is a low profile, automotive grade molding compound that is suitable for Injection, Compression or Transfer molding operations. BMC 324 can be metallized directly, without an initial base-co.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | ASTM D638 |
Arkema Group Kynar Super Flex® 2500 PVDF Copolymer
(discontinued **) Copolymer Series, Kynar® components are used extensively in the high purity semiconductor market, the pulp and paper industry, nuclear waste processing, and the general chemical processing industry.. |
|||
Tensile Strength, Ultimate | 27.6 - 45.0 MPa | 4000 - 6530 psi | Average value: 36.4 MPa Grade Count:28 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Stainless Steel Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Stainless Steel Fiber Filled". Each property range of values repo.. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 40S Chlorosulfonated Polyethylene Rubber, General Description
(discontin Product form is white, odorless chips. Distinguishing Feature: Low viscosity polymer. Improves processing of dry stiff stocks.35 % Chlorine Content. 1% Sulfur Content. Excellent Abrasion Resista.. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 4085 Chlorosulfonated Polyethylene Rubber, General Description
(disconti Product form is white, odorless chips. Distinguishing Feature: High polymer viscosity. Good green strength. Improves processing of soft or highly extended stocks.36 % Chlorine Content. 1% Sulfur.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | |
Sylvin Technologies 9604-95C Clear PVC for Injection Molding Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | TM R050-36 |
Resinlab® EP1046FG Clear Electronic Grade Epoxy Encapsulant Resinlab™ EP1046FG Clear is a two part unfilled very fast curing electronic grade epoxy encapsulant designed for small castings (less than 25 grams). It cures very quickly with low exotherm to a to.. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 45 Chlorosulfonated Polyethylene Rubber, General Description
(discontinu Product form is white, odorless chips. Distinguishing Feature: High uncured strength. Good heat resistance. Good low temperature flexibility.24 % Chlorine Content. 1% Sulfur Content. Excellent .. |