Polymer Property : Tensile Strength at Break = 4000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 27.6 MPa | 4000 psi | 2 in/min; ASTM D638 |
| RheTech Products T30P100-00 30% Talc Reinforced Polypropylene, Natural Applications: Headlamp housingsI/P componentsHVAC ductworkInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | 2 in/min; ASTM D638 |
| RheTech Products T40P100-01A 40% Talc Reinforced Polypropylene, Black Applications: Wire troughBracketsConsolesFan shroudsFuse panel boxInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D4894 |
| 3M Dyneon™ CCX1029 PTFE, 10% Carbon Fiber Filled
(discontinued **) Type I, non-free-flowing.Typical Applications: Finished or semi-finished parts: sheets, rods, tubes, billets for skiving of films or machining into complex shapes.Information provided by the Dyneon .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 18% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Albis Plastics Cellulose Acetate Propionate CP801 (UV Inhibitor Added), 18% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D412 |
| Huntsman KRYSTALFLEX® PE 429 Polyurethane Optical Aliphatic Film Key Properties:Moisture ResistanceChemical CompatibilityCooler ProcessingHigher AdhesionMultiple Design OptionNo special storage requiredInformation provided by Alliance Polymers |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | 2 in/min.; ASTM D638 |
| Ineos G36-10-150 HDPE G36-10-150 is a medium density hexene copolymer polyethylene resin designed for the blown geomembrane sheet process. This resin is especially well suited for the production of textured geomembranes... |
|||
| Tensile Strength at Break | 27.6 - 31.0 MPa | 4000 - 4500 psi | |
| ITW Plexus Plexusâ„¢ MA310 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Use with "difficult to bond" plastics, high strength.Information provided by Illinois Tool Works. |
|||
| Tensile Strength at Break | 27.6 - 31.0 MPa | 4000 - 4500 psi | |
| ITW Plexus Plexusâ„¢ MA350 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Low viscosity adhesive, high strength, especially suitable for battery case applications.Informati.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| LyondellBasell Alathon® H5618 High Density Polyethylene ApplicationsALATHON H 5618 provides easy processing characteristics and exhibits excellent toughness properties and color as well as low odor and good processing stability. Typical applications inc.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| A. Schulman POLYTROPE™ TPP 408 Blow Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 408 is a blow molding grade olefinic thermoplastic elastomer. This elastomer is specifically designed for flexible, automotive under-hood air ducts. This product contains .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | 2.0 in/min; ASTM D412 |
| Teknor Apex Telcar® TL-1377A Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets P.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| A. Schulman POLYTROPE™ TPP 403 Blow Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 403 is a blow molding grade olefinic thermoplastic elastomer. This elastomer is specifically designed for flexible, automotive under-hood air ducts. This product contains .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Total 5502 HDPE, blow molding, pipe Drug Master File listed; USP Class VI approved; FDA compliant; UL 94HB/746 certified |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company EMI 661 FR Acrylonitrile Butadiene Styrene (ABS), Stainless Steel Fiber - Electrically Conductive - EMI/RFI/ESD Protection - Flame Retardant |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| A. Schulman COMTUF® 420 Impact Modified PBT Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| A. Schulman COMTUF® 420 Impact Modified PBT Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company EMI 662 FR Acrylonitrile Butadiene Styrene (ABS), Stainless Steel Fiber - Electrically Conductive - EMI/RFI/ESD Protection - Flame Retardant |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| A. Schulman POLYTROPE™ TPP 408 Blow Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 408 is a blow molding grade olefinic thermoplastic elastomer. This elastomer is specifically designed for flexible, automotive under-hood air ducts. This product contains .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company RTP 299 A X 106739 Nylon 6 (PA), High Gravity Compound |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Eastman Tenite 307E4000018 Propionate Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties if Tenite cellulosi.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 Die C |
| 3M Scotch-Weld™ TE200 Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as .. |
|||
| Tensile Strength at Break | >= 27.58 MPa | >= 4000 psi | Sintered Molding; ASTM D4894-98a |
| 3M Dyneon™ TF 1645 PTFE Meets ASTM D4894 Type IV, Grade 2 resinMolding and ram extrusion powder very good free-flow propertiesGood metering propertiesGood mold filling behaviorGood electrical and mechanical propertiesUsed .. |
|||
| Tensile Strength at Break | 27.6 - 31.0 MPa | 4000 - 4500 psi | TM R050-36 |
| Resinlab® EP1195 Flame Retardant Epoxy Casting Resin Resinlab™ EP1195 is a low viscosity, fast gelling, flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Laboratories Inc., (File # E1.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company RTP 100 FR Polypropylene (PP), Flame Retardant - Non-PBDE/PBB - UL94 V-0 |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Chesterton MRS 10 Metal Rebuilding System Description: A reinforced composite for the repair and protection of metal surfaces. It is machinable with excellent compressive strength, chemical resistance It is non-sagging, non-shrinking and 10.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Plastics Group Polifil® RMT-20V 20% Talc-Reinforced Polypropylene, High Impact, UV Stabilized Polifil® RMT-V series compounds are high impact, UV stabilized polypropylenes reinforced with asbestos-free talc. In addition to high impact strength, they possess a high flex modulus and the abili.. |
|||
| Tensile Strength at Break | >= 27.58 MPa | >= 4000 psi | Sintered Molding; ASTM D4894-98a |
| 3M Dyneon™ TF 1620 PTFE Meets ASTM D4894 Type IV, Grade 2 resinSemi-free-flowing compression molding powderHigh bulk densityGood for large billets and thin walled isostatic moldingsVery dense polymer structure, similar to .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| A. Schulman POLYTROPE™ TPP 403 Blow Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 403 is a blow molding grade olefinic thermoplastic elastomer. This elastomer is specifically designed for flexible, automotive under-hood air ducts. This product contains .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company PermaStat® 200 Nylon 6/6 (PA), Permanently Anti-static - ESD Protection |
|||