Ineos TUB 121N HDPE
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | Ineos Olefins & Polymers USA |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos TUB 121N HDPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TUB121N is a natural high density bimodal polyethylene copolymer designed for extrusion of potable water, natural gas, industrial, and mining pipe. When blended with an approved black concentrate, the resulting TUB 121 formulation has NSF Standard 14 certification and complies with ANSI/NSF Standard 61 health effects requirements. TUB 121 is recognized by the Plastic Pipe Institute as having a pipe material designation code of PE 4710 and PE 100.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9485 g/cc | 0.03427 lb/in³ | ASTM D4883 |
| Environmental Stress Crack Resistance | >= 5000 hour | >= 5000 hour | Condition C; ASTM D1693 |
| High Load Melt Index | 8.5 g/10 min @Load 21.6 kg, Temperature 190 °C |
8.5 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| PENT | >= 10000 hour | >= 10000 hour | Notched Tensile; ASTM F1473 |
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength at Break | 37.9 MPa | 5500 psi | 2 in/min; ASTM D638 |
| Tensile Strength, Yield | 24.99 MPa | 3625 psi | 2 in/min; ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.03 GPa | 150 ksi | 2% Secant-Method 1; ASTM D790 |
| Izod Impact, Notched | 4.81 J/cm | 9.00 ft-lb/in | ASTM D256 |
| Hydrostatic Design Basis | 6.89 MPa | 1000 psi | at 60°C; ASTM D2837 |
| 11.0 MPa @Temperature 23.0 °C |
1600 psi @Temperature 73.4 °F |
ASTM D2837 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Brittleness Temperature | <= -118 °C | <= -180 °F | ASTM D746 |
| Decomposition Temperature | >= 220 °C | >= 428 °F | Thermal Stability; ASTM D2513/D3350 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cell Classification | 445574A | |
| Process | Pipe Extrusion | |
| Region | US & Canada | Bamberger Polymers Distribution |
Users viewing this material also viewed the following:
- MV Labs LU870 Lu2(C2O4)3·6H2O Lutetium oxalate hydrate
- PolyOne Nymax™ 600 Zip 0 Black 13 Polyamide 6 Alloy (Nylon 6 Alloy)
- PolyOne Bergadur™ PB40 G15 blue Polybutylene Terephthalate (PBT)
- Multibase Dow Corning® MB50-010 Siloxane Additive
- Latrobe Lescalloy® 4340 VAC-ARC ; 10.5" square High Strength Alloy Steel
- A. Schulman SCHULAMID® 66 MK20HI 20% Mineral Reinforced, Impact Modified Nylon 66
- Zylog Hipolyene® 8025 HC Thermoplastic Polyolefin & PP Compound
- Hippe PF CC 31 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod
- PolyOne Lubri-Tech™ MP-000/15T Modified PPO - 15% PTFE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved