- Polymer Property : Tensile Strength at Break = 27.6 MPa
Polymer Property : Tensile Strength at Break = 27.6 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 27.6 MPa | 4000 psi | 2 in/min; ASTM D638 |
| RheTech Products T30P100-00 30% Talc Reinforced Polypropylene, Natural Applications: Headlamp housingsI/P componentsHVAC ductworkInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | 2 in/min; ASTM D638 |
| RheTech Products T40P100-01A 40% Talc Reinforced Polypropylene, Black Applications: Wire troughBracketsConsolesFan shroudsFuse panel boxInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | TM R050-36 |
| Resinlab® EP965LVLX Black Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP965LVLX Black is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It cures at room temperature to a tough, semi-rigid polymer. It has .. |
|||
| Tensile Strength at Break | >= 27.6 MPa | >= 4000 psi | ASTM D4894 |
| 3M Dyneon™ 1750 PTFE Powder
(discontinued **) Type II PTFE. The unique properties of polytetrafluoroethylene (PTFE) makes it an indispensable material for modern industry. PTFE offers the following exceptional characteristics:Inert to a wide r.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D4894 |
| 3M Dyneon™ 1641 PTFE Powder
(discontinued **) Type IV, gr. 2 PTFE. The unique properties of polytetrafluoroethylene (PTFE) makes it an indispensable material for modern industry. PTFE offers the following exceptional characteristics:Inert to a.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D4894 |
| 3M Dyneon™ TR 1105 PTFE
(discontinued **) Ideal for thin wall ram extrusion productsReduces cold flow and melt viscosityLower permeabilityLower porosityWeldableExcellent product smoothnessIncreased machine outputInformation provided by Dyne.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 18% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| LyondellBasell Alathon® L5332CP High Density Polyethylene, Blow Molding Grade ALATHON L5332CP is bimodal molecular weight distribution, fractional melt index HDPE resin that exhibits an exceptional balance of environmental stress crack resistance and stiffness. Typical applic.. |
|||
| Tensile Strength at Break | 27.6 - 31.0 MPa | 4000 - 4500 psi | |
| ITW Plexus Plexusâ„¢ MA350 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Low viscosity adhesive, high strength, especially suitable for battery case applications.Informati.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| LyondellBasell Alathon® H5618 High Density Polyethylene ApplicationsALATHON H 5618 provides easy processing characteristics and exhibits excellent toughness properties and color as well as low odor and good processing stability. Typical applications inc.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| A. Schulman COMTUF® 420 Impact Modified PBT Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | |
| Master Bond EP51AN Thermally Conductive Adhesive System Description: Master Bond Polymer Adhesive EP51AN is a two component, thermally conductive, electrically insulating epoxy adhesive, sealant, and coating with a 1:1 mix ratio by weight or volume. This.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| A. Schulman POLYTROPE™ TPP 403 Blow Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 403 is a blow molding grade olefinic thermoplastic elastomer. This elastomer is specifically designed for flexible, automotive under-hood air ducts. This product contains .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company EMI 662 FR A Acrylonitrile Butadiene Styrene (ABS); Stainless Steel Fiber - Electrically Conductive - EMI/RFI/ESD Protection - Flame Retardant |
|||
| Tensile Strength at Break | 27.6 MPa @Thickness 3.20 mm |
4000 psi @Thickness 0.126 in |
Die C; 20 in/min (500 mm/min); ASTM D 412 |
| RTP Company ESD C 1200 T-70D Ether-based Thermoplastic Polyurethane Elastomer; Electrically Conductive - ESD Protection |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company RTP 100 FR LF Polypropylene (PP), Low Flow - Flame Retardant - UL94 V-0 |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company RTP 101 HI Z Polypropylene (PP) Glass Fiber - Impact Modified - FDA Compliant Ingredients |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| A. Schulman POLYTROPE™ TPP 408 Blow Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 408 is a blow molding grade olefinic thermoplastic elastomer. This elastomer is specifically designed for flexible, automotive under-hood air ducts. This product contains .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company EMI 662 FR Acrylonitrile Butadiene Styrene (ABS), Stainless Steel Fiber - Electrically Conductive - EMI/RFI/ESD Protection - Flame Retardant |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company PermaStat® 100 LE Polypropylene (PP), Permanently Anti-static - ESD Protection - Low Extractables |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company RTP 100 TFE 20 Polypropylene (PP), PTFE Lubricated |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| A. Schulman POLYTROPE™ TPP 403 Blow Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 403 is a blow molding grade olefinic thermoplastic elastomer. This elastomer is specifically designed for flexible, automotive under-hood air ducts. This product contains .. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company RTP 2099 X 115382 C Bio-Based Polylactic Acid (PLA); PLA-HDPE Blend - 39% Renewable Resource Content For detailed processing information, see the PLA Molding Guide on the RTP Company website. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company RTP 299 A X 106739 Nylon 6 (PA), High Gravity Compound |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Eastman Tenite 307E4000018 Propionate Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties if Tenite cellulosi.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | vs. aluminum; 60 s set time |
| Elmer's Products Aron Alpha® 102 Cyanoacrylate Adhesive (Industrial Krazy Glue™) Superior tensile and shear strengths, well suited for metal bondingMedium gap fill. Methyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Poor on porous sub.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 Die C |
| 3M Scotch-Weld™ EZ250120 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive (PUR) Easy 250 Wood Adhesive is 100% solid, warm temperature applied, moisture curing urethanes. This product bonds well to wood and wood bases surfaces as w.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Americas Styrenics STYRON® 487 High Impact Polystyrene Product CharacteristicsGood TrimmabilityToughnessHeat resistanceFood Contact CompliantUL Classification 94HBTypical ApplicationsLidsAppliancesPackaging/disposablesHousewaresInformation provided by A.. |
|||
| Tensile Strength at Break | 27.6 - 31.0 MPa | 4000 - 4500 psi | TM R050-36 |
| Resinlab® EP1195 Flame Retardant Epoxy Casting Resin Resinlab™ EP1195 is a low viscosity, fast gelling, flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Laboratories Inc., (File # E1.. |
|||
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 |
| RTP Company RTP 3503 Fluorinated Ethylene Propylene (FEP), Glass Fiber |
|||