Polymer Resources TP-G30 Polybutylene Terephthalate, 30% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources TP-G30 Polybutylene Terephthalate, 30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
ASTM D792
Linear Mold Shrinkage 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
ASTM D955
Melt Flow 8.0 - 20 g/10 min

@Load 2.16 kg,
Temperature 250 °C
8.0 - 20 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 117 MPa
17000 psi
ASTM D638
Tensile Strength, Yield 117 MPa
17000 psi
ASTM D638
Flexural Strength 186 MPa
27000 psi
ASTM D790
Flexural Modulus 6.89 GPa
1000 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature 22.8 °C
1.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 202 °C
395 °F
ASTM D648
UL RTI, Electrical 75.0 °C

@Thickness 1.50 mm
167 °F

@Thickness 0.0591 in
UL 746
75.0 °C

@Thickness 3.00 mm
167 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 1.50 mm
167 °F

@Thickness 0.0591 in
UL 746
75.0 °C

@Thickness 3.00 mm
167 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 75.0 °C

@Thickness 1.50 mm
167 °F

@Thickness 0.0591 in
UL 746
75.0 °C

@Thickness 3.00 mm
167 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Electrical Properties Metric English Comments
Comparative Tracking Index 400 - 600 V
400 - 600 V
UL 746
Hot Wire Ignition, HWI 30 - 60 sec

@Thickness 1.50 mm
30 - 60 sec

@Thickness 0.0591 in
UL 746
60 - 120 sec

@Thickness 3.00 mm
60 - 120 sec

@Thickness 0.118 in
UL 746
High Amp Arc Ignition, HAI 30 - 60 arcs

@Thickness 1.50 mm
30 - 60 arcs

@Thickness 0.0591 in
UL 746
30 - 60 arcs

@Thickness 3.00 mm
30 - 60 arcs

@Thickness 0.118 in
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 238 - 254 °C
460 - 490 °F
Middle Barrel Temperature 243 - 260 °C
470 - 500 °F
Front Barrel Temperature 249 - 266 °C
480 - 510 °F
Melt Temperature 232 - 260 °C
450 - 500 °F
Mold Temperature 65.6 - 87.8 °C
150 - 190 °F
Drying Temperature 116 - 121 °C
240 - 250 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0005