Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GMF 600 A 40 Natural Polyamide 6 (Nylon 6) The Nymax® 600 Series of mineral-reinforced nylon 6 compounds have been specifically developed to provide an excellent balance of physical property performance and durability, with improved surface.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GMF 604 40 UV Black 148 Polyamide 6 (Nylon 6) The Nymax® GMF 600 Series of compounds are based upon nylon 6 resins and select combinations of glass fiber and mineral reinforcements offering a unique balance of physical property and part perfor.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Polymer Resources TPSF-G30 Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inf.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N1033STL Nylon 6/6 (DAM) Information provided by Ravago. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | 5.1 mm/min; ASTM D638 |
PolyOne Edgetek® PC-30GF/000 BLACK Polycarbonate (PC) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for .. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GF 1200 A 13 Natural Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ X GMF 604 40 UV Black 148 rev 4 Polyamide 6 (Nylon 6) The Nymax® GMF 600 Series of compounds are based upon nylon 6 resins and select combinations of glass fiber and mineral reinforcements offering a unique balance of physical property and part perfor.. |
|||
Tensile Strength at Break | 117 MPa @Thickness 3.17 mm |
17000 psi @Thickness 0.125 in |
ASTM D638 |
PTS 30GFR-BK PBT- Flame Retardant, 30% Glass Filled PBT Black Resin Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon DE002E PC (Europe-Africa-Middle East) LNP* STATKON* DE002E is a compound based on Polycarbonate resin containing Carbon Fiber. Added features include; Easy Molding.This data was supplied by SABIC-IP for the Europe-Africa-Middle East reg.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DX06500 PC (Asia Pacific) LNP* Stat-kon* DX06500 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® HR426 PBT (Asia Pacific) AUTOMOTIVE. 30% GR, hydrolytically stable PBT. Excellent strength, stiffness and dimensional stability. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® SHF436HR PBT (Asia Pacific) PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DF006RXQ PC LNP* THERMOCOMP* DF006RXQ is a compound based on Polycarbonate resin containing 30% Glass Fiber. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC (Europe-Africa-Middle East) LNP* Thermocomp* Lexan_LGK3020 compound is a glass reinforced, flame retardant material. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RFZ22S PA 66 (Asia Pacific) LNP* Thermocomp* RFZ22S is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP WF004 PBT LNP* THERMOCOMP* WF004 is a compound based on PBT resin containing 20% Glass Fiber. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Chase Plastics CP Pryme® N320L (Dry) Nylon 6, 20% Glass Fiber Reinforced, Lubricated, Recycled Content Features: LubricatedRecycled contentForm: PelletsInformation provided by Chase Plastics. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Chase Plastics CP Pryme® NN113GL (DAM) Nylon 66, 13% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Chase Plastics CP Pryme® PC330GR Polycarbonate (Utility Grade), 30% Glass Fiber Reinforced, Mold Release Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | DIN EN ISO 527 |
Wolf Kunststoff ZEDEX® ZX-324V1T A3H PEEK Polymer, Reinforced Main Characteristics: High resilience; High elasticity; Low permanent deformation; Stress resistant; High strength at temperatures above 140 ° CApplications: Shipbuilding; Chemical Engineering; Aut.. |
|||
Tensile Strength at Break | 117 MPa | 16900 psi | ASTM D638 |
A. Schulman ComAlloy® E-17036 Glass Fiber Reinforced High Heat Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Polymer Resources PCSF-FRG20 Polycarbonate, 20% Glass Reinforced Structural Foam Grade Polycarbonate, 20% Glass Reinforced Structural Foam GradeFeatures: • Flame Retardant • Foamable • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mechanical and thermal testing con.. |