PolyOne Nymax™ GF 600 A 33 HS7 DX9 Black Polyamide 6 (Nylon 6)

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer PolyOne Corporation
Trade Name Nymax™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Nymax™ GF 600 A 33 HS7 DX9 Black Polyamide 6 (Nylon 6).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing enhanced surface appearance versus nylon 6/6 compounds. These materials are available in a broad range of reinforcement levels depending upon stiffness characteristics desired and have been formulated to offer ease of processing in most standard thermoplastic processing equipment.Molded Test Bars: Dry as MoldedInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.38 g/cc
1.38 g/cc
ASTM D792
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 0.90 %
0.90 %
@ 24 hrs; ASTM D570
1.0 %
1.0 %
24h/23C; ISO 62
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
ISO 294-4
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 172 MPa
24900 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Strength, Yield 0.965 MPa
140 psi
ISO 527-2
165 MPa
23900 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 4.0 %
4.0 %
ISO 527-2
Elongation at Yield 3.0 %
3.0 %
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 8.27 GPa
1200 ksi
ASTM D638
8.30 GPa
1200 ksi
ISO 527-2
Flexural Strength 1.52 MPa
220 psi
ISO 178
241 MPa
35000 psi
ASTM D790
Flexural Modulus 8.27 GPa
1200 ksi
ASTM D790
8.30 GPa
1200 ksi
ISO 178
Izod Impact, Notched 1.10 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
2.06 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Izod Impact, Notched (ISO) 18.0 kJ/m²
8.57 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Annealed; ISO 75-2/A
206 °C

@Thickness 3.18 mm
403 °F

@Thickness 0.125 in
Annealed; ASTM D648
Processing Properties Metric English Comments
Mold Temperature 48.9 - 93.3 °C
120 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Additive Heat Stabilizer
Appearance Black
Automotive Specifications CHRYSLER MS-DB41 CPN2625
Features General Purpose
Good Weather Resistance
Heat Stabilized
Filler / Reinforcement Glass Fiber Reinforcement, 33% Filler by Weight
Forms Pellets
Generic Material Nylon 6
Generic Name Polyamide 6 (Nylon 6)
Processing Method Injection Molding
Regional Availability North America
South America
Uses Automotive Applications
Construction Applications
Consumer Applications
General Purpose
Industrial Applications