Polymer Property : Tensile Modulus = 8.30 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 8.30 GPa
1200 ksi
ISO 527-2
PolyOne Nymax™ GF 600 A 33 HS7 DX9 Black Polyamide 6 (Nylon 6)
The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing en..
Tensile Modulus 8.30 GPa
1200 ksi
ISO 527, ASTM D638
Nilit Nilamid A G5 FR PH2 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Red Phosphorous)
Description: Nilamid A G5 FR PH2 combines flame retardancy with outstanding mechanical performance. This product has a complete yellow card, with RTI and CTI listings. The formulation has been optim..
Tensile Modulus 8.30 GPa
1200 ksi
Radici Radilon® A RV250 (dry) Nylon 66
Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov..
Tensile Modulus 8.30 GPa

@Temperature 23.0 °C
1200 ksi

@Temperature 73.4 °F
ISO 527-2/1
PolyOne Bergamid™ B65 G30 black IG Polyamide 6 (Nylon 6)
Information provided by PolyOne
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Shell Carilon® DP R1130 Polyketone, 30% Glass Fiber Reinforced  (discontinued **)
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON® Thermoplastic Polymer DP R1130 is a 30 percent glass fiber reinforced compound based on a developmental e..
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Shell Carilon® DB6G6A10 Polyketone, 30% Glass-Reinforced General-Purpose Injection Molding Grade  (discontinue
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DB6G6A10 is a 30 percent short glass-fiber-reinforced, general purpose injection molding grade, wit..
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, Dry As Molded  
AMODEL A-1115 HS resin is a 15% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, and high tensile strength. Excellent cre..
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, at 50% RH  (dis
AMODEL A-1115 HS resin is a 15% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, and high tensile strength. Excellent cre..
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Solvay Specialty Polymers Amodel® A-1240 HS Polyphthalamide (PPA) Resin, 40% Mineral Reinforced, at 50% RH  (d
AMODEL A-1240 polyphthalamide (PPA) resins are 40% mineral filled resins that have high deflection temperature, flexural modulus, and tensile strength. They mold with low warpage, have excellent di..
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
RTP Company RTP 4505 TFE 15 Aliphatic Polyketone, Glass Fiber 30% - PTFE 15%  (discontinued **)
Properties and average values of injection molded specimens; data provided by RTP Company.This product has been discontinued, please contact RTP Company regarding alternate grades.
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Plenco Valite 424 Novolac Phenolic, Granular, Injection Molded  (discontinued **)
This Valite product has been replaced by Plenco 2424. Data provided by Plenco.VALITE 424 is a black, two stage, general purpose phenolic molding compound. It has a good balance of properties for a ..
Tensile Modulus 8.30 GPa
1200 ksi
ISO 527 Type 1A
Solvay TECHNYL® C 216 V45 PA6, 45% glass fiber, Conditioned
Description: Polyamide PA6, reinforced with 45% of glass fiber, for injection molding.Available in: EuropeProduct Applications: TECHNYL C 216 V45 has been optimized to have high impact strength, a n..
Tensile Modulus 8.30 GPa
1200 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics SABIC STAMAX 40YM240 PP
SABIC® STAMAX 40YM240 is a 40% long glass fiber reinforced polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 16497161...
Tensile Modulus 8.30 GPa
1200 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON RX06001 PA 66 (Europe-Africa-Middle East)
LNP* Stat-kon* RX06001 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Easy Molding, High Impact, Electrically Conductive.
Tensile Modulus 8.30 GPa
1200 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DX06313I PC (Asia Pacific)
DX06313I is 30% glass fiber reinforced, impact modified polycarbonate resin. High flow and good ductility.
Tensile Modulus 8.30 GPa
1200 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF005 PA 66
LNP* THERMOCOMP* RF005 is a compound based on Nylon 66 resin containing 25% Glass Fiber.
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Sumitomo Bakelite Durez® 118 Phenolic, Injection Grade
Durez 118 Black Phenolic is a two-stage, asbestos free, general purpose molding material. It exhibits improved impact strength and resistance to flexural fatigue for demanding automotive, electrica..
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Sumitomo Bakelite Durez® 31906 Phenolic, Compression Grade
Durez 31906 Black Phenolic is an asbestos free, medium impact, molding compound. It is designed for applications where additional mechanical strength is required.Information provided by Sumitomo Ba..
Tensile Modulus 8.30 GPa
1200 ksi
1 mm/min; ISO 527-1
Sax Polymers SAXAMID 226F4RY01 Nylon 6.6, 20% Glass Fiber
SAXAMID 226F4RY01 is a polyamide 6.6 injection-molding-grade reinforced with 20% glass fibers. It has a halogen-free flame retardant.Information provided by SAX Polymers
Tensile Modulus 8.30 GPa
1200 ksi
ISO 527 Type 1A
Solvay TECHNYL® C 246SI V30 PA6, 30% glass filled, DRY
Description: Polyamide 6, reinforced with 30 % of glass fiber, with high impact resistance, for injection molding.Available in: Asia Pacific , Europe and North AmericaProduct Applications: Having go..
Tensile Modulus 8.30 GPa
1200 ksi
ASTM-D790
Polyram PlusTek PA4801G6 Nylon 6.6, 30% Glass Fiber Reinforced, PTFE lubricated
30% glass fiber reinforced, PTFE lubricated polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Tensile Modulus 8.30 GPa
1200 ksi
cond; ISO 527-1/-2
DSM Novamid® 1010GN2-30 NAT/BK37 PA6-GF30 FR(17)
30% Glass Reinforced, Flame Retardant
Tensile Modulus 8.30 GPa

@Temperature 180 °C
1200 ksi

@Temperature 356 °F
ISO 527-1/-2
DSM Stanyl® TW200B6 PA46-CF30
30% Carbon Reinforced, Heat Stabilized, Lubricated
Tensile Modulus 8.30 GPa

@Temperature 80.0 °C
1200 ksi

@Temperature 176 °F
ISO 527-1, -2
Celanese Celstran® PP-GF50-0403 P10 PP, 50% Glass Reinforced
Material code according to ISO 1043-1: PPInformation provided by Celanese
Tensile Modulus 8.30 GPa
1200 ksi
1mm/min; ISO 527
BASF Ultramid® 8267G HS BK-102 15/25% Glass/Mineral Filled PA6 (Dry)
Ultramid 8267G HS BK-102 is a heat stabilized, black pigmented, 40% mineral and glass fiber reinforced nylon 6 injection molding compound. It possesses a balance of engineering properties in combin..
Tensile Modulus 8.30 GPa
1200 ksi
50mm/min; ISO 527-2/1A
Celanese VECTRA S625 LCP, 25% Specialty
Low friction and wear resistance.Information provided by Celanese
Tensile Modulus 8.30 GPa
1200 ksi
Elasticity; ISO 527-1/-2
BASF Ultrason S 2010 G6 30% Glass Filled PSU
Ultrason S 2010 G6 is a 30% glass reinforced, medium viscosity injection molding PSU grade with high rigidity and strength.
Tensile Modulus 8.30 GPa
1200 ksi
50mm/min; ISO 527-2/1A
Celanese CELANEX 531HS PBT, Glass Reinforced
Celanex 531HS is a 30% fiberglass reinforced PBT which has an excellent balance of mechanical properties and processability. Celanex 531HS is specifically designed to exhibit excellent thermal shoc..
Tensile Modulus 8.30 GPa
1200 ksi
50mm/min; ISO 527-2/1A
Celanese Celstran® PA66-GF20-02P11/12 Nylon 66, 20% Glass Reinforced
Nylon 66 reinforced by 20 weight percent long glassInformation provided by Celanese
Tensile Modulus 8.30 GPa
1200 ksi
ASTM D638
Plenco 7579 Phenolic, Granular, Injection Molded
PLENCO 07579 is a fast curing, woodflour filled, novolac phenolic molding compound, formulated for industrial applications that do not require a smooth finish. UL recognized under component file E40..