Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 172 MPa | 24900 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GF 604 35 HS Natural Polyamide 6 (Nylon 6) The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing en.. |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | ASTM D638 |
Performance Polymers IPS II PPL-C4219 PEKK (Polyetherketoneketone) Linear Wear Grade Black pellets; Carbon fiber/PTFE/Graphite compoundInformation provided by Infinite Polymer System II. |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | ASTM D638 |
PolyOne Stat-Tech™ NN-20CF/000 Black HS Polyamide 66 (Nylon 66) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound.. |
|||
Tensile Strength at Break | 172 - 207 MPa | 25000 - 30000 psi | Copper butt joint |
Lucas-Milhaupt BRAZE 250 Silver Based Cadmium Free Filler Metal Characteristics:Braze 250 is an intermediate temperature silver brazing alloy with a long (325EF/180EC) melting range. It has a tendency to liquate (i.e. separate into low and high melting constitu.. |
|||
Tensile Strength at Break | 172 - 207 MPa | 25000 - 30000 psi | Copper butt joint |
Lucas-Milhaupt BRAZE 600 Silver Based Cadmium Free Filler Metal Characteristics: Braze 600 is a copper rich eutectiferous alloy, the eutectiferous portion of which is molten at 1300EF (705EC), about 25EF before the entire composition is completely fluid. Thus t.. |
|||
Tensile Strength at Break | 172 - 207 MPa | 25000 - 30000 psi | Brass butt joint |
Lucas-Milhaupt BRAZE 700 (Medium) Silver Based Cadmium Free Filler Metal Characteristics: This alloy is a intermediate silver brazing filler metals with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through their mel.. |
|||
Tensile Strength at Break | 172 - 207 MPa | 25000 - 30000 psi | Copper butt joint |
Lucas-Milhaupt BRAZE 750 (Hard) Silver Based Cadmium Free Filler Metal Characteristics: This alloy is a intermediate silver brazing filler metals with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through their mel.. |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | ASTM D638 |
Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA), 33% Glass Fiber (Conditioned) Amodel® AS-4133 L polyphthalamide (PPA) a 33% glass reinforced, lubricated, structural grade of polyphthalamide (PPA) that offers fast cycle times and is hot water moldable. Typical applications .. |
|||
Tensile Strength at Break | 172 MPa | 25000 psi | ASTM D638 |
Techmer ES Electrafil® J-1305/CF/30/TF/15 BK PPS |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM SF2350 PEI Blend (Asia Pacific) High flow Ultem blends for thin wall application |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DE006 PC (Europe-Africa-Middle East) LNP* Stat-kon* DE006 is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Stat-kon OEL36A PPS LNP* Stat-Kon* OEL36A is a compound based on Polyphenylene Sulfide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This .. |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | 0.2 in/min; ASTM Test |
BASF Ultramid® 1703-2 BK ND3007 25% Glass Filled PA66 (Dry) Ultramid 1703-2 BK ND3007 is a 25% glass reinforced, heat stabilized injection molding nylon 6/6. |
|||
Tensile Strength at Break | 172 MPa | 25000 psi | ASTM D638 |
Techmer Lehvoss Compounds Luvotech™ J-4/30 BK PA6/12
(discontinued **) Techmer Lehvoss Compounds, a JV between Techmer ES and Lehmann&Voss&Co. has been terminated. |
|||
Tensile Strength at Break | 172 MPa | 25000 psi | ASTM D638 |
Techmer Lehvoss Compounds Luvotech™ J-4/35 BK223 PA6/12
(discontinued **) Techmer Lehvoss Compounds, a JV between Techmer ES and Lehmann&Voss&Co. has been terminated. |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | Type I, 5 mm/min; ASTM D638 |
LNP ULTEM® SMU5836 Polyetherimide, 30% Carbon Fiber Reinforcement
(discontinued **) High modulus with shielding/ conductive characteristics for high-heat applications.Features: Electrically Conductive, High Heat Resistance, High StrengthForms: PelletsProcessing Method: Injection Mo.. |