Overview of materials for Polybutylene Terephthalate (PBT), Carbon Black Filled

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Carbon Black Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polybutylene Terephthalate (PBT), Carbon Black Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Carbon Black Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.33 - 1.67 g/cc
0.0480 - 0.0603 lb/in³
Average value: 1.45 g/cc Grade Count:16
Linear Mold Shrinkage 0.000500 - 0.00910 cm/cm
0.000500 - 0.00910 in/in
Average value: 0.00366 cm/cm Grade Count:9
Linear Mold Shrinkage, Transverse 0.00800 - 0.0110 cm/cm
0.00800 - 0.0110 in/in
Average value: 0.00958 cm/cm Grade Count:3
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 40.0 - 175 MPa
5800 - 25400 psi
Average value: 105 MPa Grade Count:16
Tensile Strength, Yield 49.0 - 142 MPa
7110 - 20600 psi
Average value: 104 MPa Grade Count:6
Elongation at Break 1.00 - 7.00 %
1.00 - 7.00 %
Average value: 3.03 % Grade Count:16
Modulus of Elasticity 2.28 - 22.4 GPa
331 - 3250 ksi
Average value: 10.4 GPa Grade Count:10
Flexural Yield Strength 68.0 - 269 MPa
9860 - 39000 psi
Average value: 157 MPa Grade Count:16
Flexural Modulus 2.06 - 22.9 GPa
299 - 3320 ksi
Average value: 11.9 GPa Grade Count:16
Izod Impact, Notched 0.214 - 0.740 J/cm
0.401 - 1.39 ft-lb/in
Average value: 0.462 J/cm Grade Count:12
Izod Impact, Unnotched 0.907 - 6.41 J/cm
1.70 - 12.0 ft-lb/in
Average value: 4.10 J/cm Grade Count:12
Falling Dart Impact 4.34 - 7.57 J
3.20 - 5.58 ft-lb
Average value: 5.62 J Grade Count:7
Thermal Properties Metric English Comments
Thermal Conductivity 1.10 - 1.20 W/m-K
7.63 - 8.33 BTU-in/hr-ft²-°F
Average value: 1.13 W/m-K Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 213 - 221 °C
415 - 430 °F
Average value: 218 °C Grade Count:5
Deflection Temperature at 1.8 MPa (264 psi) 81.0 - 216 °C
178 - 421 °F
Average value: 191 °C Grade Count:13
Flammability, UL94 HB
HB
Grade Count:3
Electrical Properties Metric English Comments
Electrical Resistivity 0.500 ohm-cm - 1e+05
0.500 ohm-cm - 1e+05
Average value: 1780 ohm-cm Grade Count:11
Surface Resistance 100 - 1.00e+10 ohm
100 - 1.00e+10 ohm
Average value: 5.56e+8 ohm Grade Count:13
Static Decay 0.0100 - 2.00 sec
0.0100 - 2.00 sec
Average value: 1.00 sec Grade Count:4
Processing Properties Metric English Comments
Nozzle Temperature 243 - 282 °C
469 - 540 °F
Average value: 256 °C Grade Count:6
Melt Temperature 238 - 282 °C
460 - 540 °F
Average value: 256 °C Grade Count:15
Mold Temperature 37.8 - 107 °C
100 - 225 °F
Average value: 81.7 °C Grade Count:15
Drying Temperature 121 - 135 °C
250 - 275 °F
Average value: 122 °C Grade Count:15
Moisture Content 0.0200 - 0.150 %
0.0200 - 0.150 %
Average value: 0.0500 % Grade Count:15
Dew Point -28.9 °C
-20.0 °F
Average value: -28.9 °C Grade Count:6
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:6
Vent Depth 0.00250 - 0.00380 cm
0.000984 - 0.00150 in
Average value: 0.00315 cm Grade Count:6