Polymer Property : Tensile Strength, Ultimate = 5800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM D638
Plaskolite Optix® CA-1000 IG Clear High Impact Acrylic Resin High impact acrylic resin, injection molding and extrusion gradeApplications: A premium impact acrylic resin particularly suited for medical and food uses. This resin offers the best impact resista..
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM D638-61T
Rotuba 860MH 686.4 Ethyl Cellulose Data provided by the manufacturer.
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM D638
Rotuba H Cellulose Acetate Property values at 50% RH.Data provided by the manufacturer.
Tensile Strength, Ultimate	40.0 - 200 MPa @Strain 0.500 - 5.00 %	5800 - 29000 psi @Strain 0.500 - 5.00 %	Average value: 93.9 MPa Grade Count:1
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25..
Tensile Strength, Ultimate	40.0 - 180 MPa	5800 - 26100 psi	Average value: 146 MPa Grade Count:26
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45..
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ISO 527
LATI LASTIROL R-V2 Polystyrene (PS) (UL94 V-2) (discontinued **) Description: Lastirol thermoplastics are polystyrene (PS) products. The Lastirols feature excellent dimensional stability, good flowability, and can be molded without any particular problem. Glass f..
Tensile Strength, Ultimate	40.0 - 60.0 MPa	5800 - 8700 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 3108/0903 Anti-static PVDF Compound (discontinued **) Key features of this grade: Anti-static, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crystall..
Tensile Strength, Ultimate	40.0 - 60.0 MPa	5800 - 8700 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 3208/0150 Anti-friction PVDF Compound (discontinued **) Key features of this grade: Anti-friction, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crysta..
Tensile Strength, Ultimate	40.0 - 224 MPa	5800 - 32500 psi	Average value: 164 MPa Grade Count:22
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler". Specific grades with carbon fiber content bet..
Tensile Strength, Ultimate	40.0 - 160 MPa @Strain 1.00 - 9.00 %	5800 - 23200 psi @Strain 1.00 - 9.00 %	Average value: 104 MPa Grade Count:1
Overview of materials for Nylon 6, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E..
Tensile Strength, Ultimate	40.0 - 160 MPa @Temperature 60.0 - 150 °C	5800 - 23200 psi @Temperature 140 - 302 °F	Average value: 104 MPa Grade Count:1
Overview of materials for Nylon 6, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E..
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM data at 5 mm/min.
BASF Capron® 8230G HS 6% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron 8230G HS is a heat stabilized, 6% nylon 6 molding compound offering improved stiffness and dimensional stability in thin sections. It exhibits a combination of strength, stiffness and perfor..
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM D638
LyondellBasell Montell 1900 UHMW Polyethylene Key Features: ultrahigh molecular weight polyethylene resin, excellent abrasion resistance, high impact strength, low coefficient of friction, good chemical resistance, low odor and taste transferAp..
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM D638
LyondellBasell Montell HB320CM UHMW Polyethylene Key Features: ultrahigh molecular weight polyethylene resin, excellent abrasion resistance, high impact strength, low coefficient of friction, good chemical resistance, low odor and taste transfer, ..
Tensile Strength, Ultimate	40.0 MPa @Temperature 22.0 Â°C	5800 psi @Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® BMC 1100 Unsaturated Polyester UP BMC 1100 is a special BMC for high strength application. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. The selection of the r..
Tensile Strength, Ultimate	40.0 MPa	5800 psi
KratonÂ® G1657 + PA-6 blend (8/12/80) Blending KRATON D and G polymers with PA significantly improves the toughness at both room and low temperatures. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A..
Tensile Strength, Ultimate	40.0 MPa	5800 psi	20 in/min, at max load; ASTM D412
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman.
Tensile Strength, Ultimate	40.0 MPa	5800 psi	20 in/min, at max load; ASTM D412
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman.
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM D412
Lubrizol Estane® ALR E72A Thermoplastic Polyurethane Type: Estane® ALR E72A is a clear aliphatic thermoplastic polyurethane (TPU).Features: Non-yellowing with good mechanical properties.Available in AmericasInformation Provided by The Lubrizol Corpor..
Tensile Strength, Ultimate	40.0 MPa	5800 psi
Colorite Polymers 1124 Clear Injection Molding Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for injection molding of various components such as drip chambers, connectors, valves, etc. The vinyl c..
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM D412
BASF Elastollan® 1154D Polyether Type Polyurethane Elastomer Recommended for injection molding. Elastollan ® 1100 series products are FDA Sec. 177.2600 compliant. Elastollan 1100 series of products are polyether-based thermoplastic polyurethanes. They exh..
Tensile Strength, Ultimate	40.0 - 100 MPa @Temperature -40.0 - 80.0 °C	5800 - 14500 psi @Temperature -40.0 - 176 °F	Average value: 71.0 MPa Grade Count:1
Overview of materials for Nylon 66, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are inclu..
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM D412
Dow PELLETHANE® 2103-75D Film Grade Thermoplastic Polyurethane Elastomer (discontinued **) Description: PELLETHANE® 2103-75D UV stabilized, polyether based thermoplastic polyurethane elastomer has excellent hydrolytic stability and excellent resistance to micro-organisms. Applications in..
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM D638
Kleerdex Kydex® 160 Acrylic/PVC Thermoplastic Sheet (discontinued **) Class I/A rated thermoplastic sheetApplications: Interior ductwork and chutes, laboratory hoods, shower/tub shrouds, acoustical applications, decorative ceilings, abuse resistant surfacing for count..
Tensile Strength, Ultimate	40.0 MPa	5800 psi	ASTM D638
Solvay Specialty Polymers Algoflon® F6 PTFE (Polytetrafluoroethylene) (discontinued **) Data provided by the manufacturer.Type II Classification. Suspension polymer powder grade recommended for compression molding and extrusion. PTFE possesses high inertness, excellent dielectric prope..