Menzolit Menzolit® HPC 1300 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® HPC 1300 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
HPC 1300 is a special SMC for high strength applications. The glass level has been selected to combine mouldability with high strength and stiffness properties in orientation direction. The reinforcement is composed of chopped, randomly distributed glass fibers and additional unchopped, continuous and lengthwise oriented glass fibers. This leads to very high stiffness and strength properties along with the unidirectional fibers. The flowabilty in orientation direction is reduced. This orientation influences flow during moulding and the anisotropic material properties have to be kept in mind during part design and part moulding. Typical applications are load bearing components, for instance bumpers and power train substructures.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | ISO 62 |
| Linear Mold Shrinkage | -0.000300 cm/cm | -0.000300 in/in | ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0025 cm/cm | 0.0025 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 415 MPa @Temperature 22.0 °C |
60200 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 415 MPa @Temperature 22.0 °C |
60200 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 1.6 % | 1.6 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 25.0 GPa | 3630 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 743 MPa @Temperature 22.0 °C |
108000 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 28.0 GPa @Temperature 22.0 °C |
4060 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Compressive Yield Strength | 370 MPa | 53700 psi | ISO 14126 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 9.62 GPa | 1400 ksi | Calculated |
| Charpy Impact, Notched | 37.2 J/cm² | 177 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.00 µm/m-°C | 3.89 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 162 °C | 324 °F | ISO 11357-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Oxygen Index | 22 % | 22 % | ISO 4589-2 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 140 - 160 °C | 284 - 320 °F | Compression moulding, matched metal die |
Users viewing this material also viewed the following:
- Nye Lubricants 741E (NG) Synthetic Oil
- Abatron AboCast 8101-1/AboCure 8101-1 Epoxy (discontinued **)
- SK Chemicals SKYTHANE® UB601 Ink Binder
- Teknor Apex Flexalloy® 9800-60 Polyvinyl Chloride Elastomer
- SABIC Innovative Plastics LNP Thermocomp DF008P PC (Asia Pacific)
- Zircar Zirconia ALK-15 Alumina Knit Textile Insulation
- Braskem KN-501 Impact Copolymer Polypropylene
- ATI Wah Chang Reactor Grade Zirconium Oxide, ZrO2
- A. Schulman POLYFLAM™ RPP 1221 Low-Blooming, General Purpose Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved