Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | >= 415 MPa | >= 60200 psi | |
MetalTek C18100 Chrome Zirc Copper High Conductivity Typical property data from forged samples.Information provided by MetalTekCast UNS C18100; Cast Grade C18100 |
|||
Tensile Strength, Ultimate | >= 415 MPa | >= 60200 psi | |
MetalTek MTEK 10-60 Cast UNS N08001 Heat Resistant Stainless Steel Not as strong as HT but high nickel content delivers excellent carburization resistance.Applications: Cyanide pots, retorts, molten lead heating elements.Information provided by MetalTekCast UNS N08.. |
|||
Tensile Strength, Ultimate | >= 415 MPa | >= 60200 psi | |
MetalTek MTEK 15-65 Cast UNS N06006 Heat Resistant Stainless Steel For severe hot gas corrosion resistance at higher temperatures.Applications: Hearth plates, muffles, roller hearths, carburizing boxes.Information provided by MetalTekCast UNS N06006; Cast Grade HX;.. |
|||
Tensile Strength, Ultimate | 415 MPa @Temperature 22.0 °C |
60200 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® HPC 1300 Unsaturated Polyester UP HPC 1300 is a special SMC for high strength applications. The glass level has been selected to combine mouldability with high strength and stiffness properties in orientation direction. The reinforc.. |
|||
Tensile Strength, Ultimate | >= 415 MPa | >= 60200 psi | |
MetalTek MTEK 70-30 UNS C96400 Nickel-Copper Alloy Information provided by MetalTek |
|||
Tensile Strength, Ultimate | 415 MPa @Temperature 870 °C |
60200 psi @Temperature 1600 °F |
|
Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Tensile Strength, Ultimate | 415 MPa @Temperature 870 °C |
60200 psi @Temperature 1600 °F |
|
Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Ultimate | 415 MPa | 60200 psi | Annealed |
Special Metals FERRY® Alloy A copper-nickel alloy used mainly for its electrical properties. It has medium-range electrical resistivity and a very low temperature coefficient of resistance (TCR). The low TCR makes the alloy .. |
|||
Tensile Strength, Ultimate | >= 415 MPa | >= 60200 psi | |
AK Steel CL 1/ SAE J1392 045 XLK, Grade 45 Cold Rolled Carbon Steel, High Strength Low Alloy Steel (HSLAS) Information provided by AK Steel |
|||
Tensile Strength, Ultimate | >= 415 MPa | >= 60200 psi | |
AK Steel SAE J1392 050 XLK, Grade 50 Aluminized Carbon Steel, High Strength Low Alloy Steel (HSLAS) Aluminized Type 1 coating contains approximately 91% aluminum and 9% silicon that is metallurgically bonded to the low-carbon steel substrate.Information provided by AK Steel |
|||
Tensile Strength, Ultimate | >= 415 MPa | >= 60200 psi | |
AK Steel ZINCGRIP® FORMABLE 50K / ASTM A1008 class 2 / SAE J1392 050 XLK, Grade 50 Electrogalvanized Carbon Steel, High Strength Low Alloy Steel (HSLAS) Information provided by AK Steel |
|||
Tensile Strength, Ultimate | >= 415 MPa | >= 60200 psi | Minimum |
ATI Allegheny Ludlum Stainless Steel AL 410S™ (UNS S41008) Allegheny Ludlum Al 410S™ stainless steel is a low-carbon modification of Type 410 stainless steel. Low carbon and optionally a small addition of titanium and /or columbium minimize austenite form.. |
|||
Tensile Strength, Ultimate | >= 415 MPa | >= 60200 psi | Minimum |
Aleris Weldural Aluminum Alloy, 100 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
Tensile Strength, Ultimate | 415 - 470 MPa | 60200 - 68200 psi | |
ArcelorMittal HSLA 320 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S315MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w.. |