Lanxess Pocan® DP 7318 000000 PBT, 17% Pigment

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer Lanxess
Trade Name Pocan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® DP 7318 000000 PBT, 17% Pigment.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, 17% white pigments, injection molding, improved light reflection, low tendency to warpInformation provided by LANXESS.
Physical Properties Metric English Comments
Bulk Density 0.900 g/cc
0.0325 lb/in³
ISO 60
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
50% RH; ISO 62
Water Absorption at Saturation 0.40 %
0.40 %
ISO 62
Viscosity Test 94 cm³/g
94 cm³/g
ISO 1628-5
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
150x105x3, 260°C / MT 80°C; 500 bar; acc. ISO 2577
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
150x105x3, 260°C / MT 80°C; 500 bar; acc. ISO 2577
Melt Flow 40.5 g/10 min

@Load 2.16 kg,
Temperature 260 °C
40.5 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ISO 1133-1
Mechanical Properties Metric English Comments
Tensile Strength at Break 57.0 MPa
8270 psi
5 mm/min; ISO 527-1,-2
Elongation at Break 10 %
10 %
5 mm/min; ISO 527-1,-2
Tensile Modulus 3.40 GPa
493 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178-A
Flexural Modulus 3.20 GPa
464 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
<= 4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 180-1A
Izod Impact, Unnotched (ISO) 110 kJ/m²

@Temperature 23.0 °C
52.3 ft-lb/in²

@Temperature 73.4 °F
ISO 180-1U
Charpy Impact Unnotched 12.5 J/cm²

@Temperature 23.0 °C
59.5 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Melting Point 225 °C
437 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO 75-1,-2
Vicat Softening Point 190 °C
374 °F
50 N; 50 °C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Shrinkage 0.200 %

@Temperature 120 °C,
Time 14400 sec
0.200 %

@Temperature 248 °F,
Time 4.00 hour
post-shrinkage, 150x105x3; acc. ISO 2577
0.200 %

@Temperature 120 °C,
Time 14400 sec
0.200 %

@Temperature 248 °F,
Time 4.00 hour
post-shrinkage, transverse, 150x105x3; acc. ISO 2577
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
Solution A; UL 746A
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Dry Time 4.00 - 8.00 hour

@Temperature 120 °C
4.00 - 8.00 hour

@Temperature 248 °F
Moisture Content 0.00 - 0.020 %
0.00 - 0.020 %
Karl Fischer test