Lanxess Durethan® DP 2131/20 W1 901317 Nylon 6, 20% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® DP 2131/20 W1 901317 Nylon 6, 20% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, injection molding grade, 20% glass fibers, better surface finish and resistance to alcoholic calcium chloride-solution than BKV 20 H2.0, weather resistance, good heat-ageing resistance
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
ISO 1183
Viscosity Test 140 cm³/g
140 cm³/g
Viscosity number; ISO 307, 1157, 1628
Melt Flow 28 g/10 min

@Load 5.00 kg,
Temperature 270 °C
 28 g/10 min

@Load 11.0 lb,
Temperature 518 °F
 Estimated using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
Conditioned; ISO 527-1/-2
150 MPa
21800 psi
ISO 527-1/-2
Elongation at Break 3.0 %
3.0 %
ISO 527-1/-2
7.0 %
7.0 %
Conditioned; ISO 527-1/-2
Tensile Modulus 4.70 GPa
682 ksi
Conditioned; ISO 527-1/-2
7.60 GPa
1100 ksi
ISO 527-1/-2
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 179/1eU
4.50 J/cm²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
6.00 J/cm²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Puncture Energy 5.00 J
3.69 ft-lb
ISO 6603-2
10.0 J
7.38 ft-lb
Conditioned; ISO 6603-2
4.00 J

@Temperature -30.0 °C
 2.95 ft-lb

@Temperature -22.0 °F
 ISO 6603-2
4.00 J

@Temperature -30.0 °C
 2.95 ft-lb

@Temperature -22.0 °F
 Conditioned; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.0 µm/m-°C
12.8 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 89.0 µm/m-°C
49.4 µin/in-°F
ISO 11359-1/-2
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 213 °C
415 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 73.0 °C
163 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
Conditioned; IEC 60093
3.00e+15 ohm-cm
3.00e+15 ohm-cm
IEC 60093
Surface Resistance 2.00e+13 ohm
2.00e+13 ohm
IEC 60093
Dielectric Constant 3.74

@Frequency 1.00e+6 Hz
 3.74

@Frequency 1.00e+6 Hz
 IEC 60250
4.1

@Frequency 100 Hz
 4.1

@Frequency 100 Hz
 IEC 60250
4.27

@Frequency 1.00e+6 Hz
 4.27

@Frequency 1.00e+6 Hz
 Conditioned; IEC 60250
9.34

@Frequency 100 Hz
 9.34

@Frequency 100 Hz
 Conditioned; IEC 60250
Dissipation Factor 0.0087

@Frequency 100 Hz
 0.0087

@Frequency 100 Hz
 IEC 60250
0.0185

@Frequency 1.00e+6 Hz
 0.0185

@Frequency 1.00e+6 Hz
 IEC 60250
0.0677

@Frequency 1.00e+6 Hz
 0.0677

@Frequency 1.00e+6 Hz
 Conditioned; IEC 60250
0.2203

@Frequency 100 Hz
 0.2203

@Frequency 100 Hz
 Conditioned; IEC 60250
Descriptive Properties Value Comments
Additives Release agent
Features Heat stabilized or stable to heat
U.V. stabilized or stable to weather
Form Pellets
ISO Shortname ISO 1874-PA 6,MHLR,14-070,GF20
Processing Injection molding
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America