Polymer Property : Tensile Strength at Break = 150 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
STN EN ISO 527-2
Plastcom SLOVAMID 6 GF 30 TS Polyamide 6, 30% Glass Fiber, Thermal Stabilization
FeaturesPA 6 for injection moulding, chemically reinforced with 30% glass fiber, heat stabilized, mouldings resistant against long-time heat impact up to 150°C. Decrease in tensile strength by 50%..
Tensile Strength at Break 150 MPa
21800 psi
Plastcom SLOVAMID 66 GF 25 FRG 5 TS PA66, 25% glass fibre, flame retardant
FeaturesPA 66 for injection moulding, chemically reinforced with 25% glass fibre and non-halogen flame retardant, with heat resistance and nonflammability, achieves V 0 in accordance with UL 94. Non..
Tensile Strength at Break 150 MPa
21800 psi
STN EN ISO 527-2
Plastcom SLOVASTER® B GF 30 Polybutylene Terephthalate, 30% Glass Fiber
FeaturesPBT for injection moulding, chemically reinforced with 30% glass fiber. Characterized by excellent properties also at low temperatures like tensile and flexural modulus, tensile strength, a..
Tensile Strength at Break 150 MPa
21800 psi
Plastcom SLOVASTER® B/E GF 30 PBT, 30% glass fibre
FeaturesPBT/PET for injection moulding, chemically reinforced with 30% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and ben..
Tensile Strength at Break <= 150 MPa
<= 21800 psi
ISO/R527
Polykemi AB POLYshine PBT D201 GF30 PBT, Glass Fiber Reinforced
Information provided by Polykemi AB
Tensile Strength at Break <= 150 MPa
<= 21800 psi
ISO/R527
Polykemi AB SCANAMID 66 A33^E F45 Nylon 66, Glass Fiber Reinforced, Elastomer Modified
Information provided by Polykemi AB
Tensile Strength at Break >= 150 MPa
>= 21800 psi
50 mm/min; ISO 527-1,2
Qualchem Danamid AFGFH-30 Polyamide 66, 30% Glass Fiber
Reinforced with glass fiber. Heat stabilized, for long-lasting use at 120-140°C.Information provided by Qualchem Zrt.
Tensile Strength at Break 150 MPa
21800 psi
50 mm/min; ISO 527-1,2
Qualchem Danamid FGF-30 Polyamide 6, 30% Glass Fiber
Reinforced with glass fiber.Information provided by Qualchem Zrt.
Tensile Strength at Break 150 MPa
21800 psi
ISO 527
Nilit FRIANYL A63 H-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break 150 MPa
21800 psi
ISO 527-1/-2
DSM Akulon® Ultraflow™ K-FKGS6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Dry)  (discontinued **
The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Strength at Break 150 MPa
21800 psi
Idemitsu Kosan Xarec® N WA 7020 SPS, 20% Glass Filled
Crystalline Polymer Blend, Glass Filled, Impact Modified. Used in Automotive Electronics applications.
Tensile Strength at Break 150 MPa
21800 psi
Conditioned; ISO 527-1/-2
Lanxess Durethan® DP BKV 60 H2.0 EF 900116 Nylon 6, 60% Glass Fiber
PA 6, injection molding grade, 60% glass fibers, low viscosity, good flowability (Easy Flow), good heat-resistanceApplication Examples: gearbox housings, spring holders, automotive door handles
Tensile Strength at Break 150 MPa
21800 psi
ISO 527-1/-2
Lanxess Pocan® B 3235 901510 PBT, 30% Glass Fiber
PBT, 30% glass fibers, injection molding
Tensile Strength at Break 150 MPa
21800 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DC006ER PC
LNP THERMOCOMP* DC006ER is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Easy Molding, Mold Release, Electrically Conductive.
Tensile Strength at Break 150 MPa
21800 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DC006ER PC (Asia Pacific)
LNP THERMOCOMP* DC006ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 150 MPa
21800 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP EF004 PEI
LNP* Thermocomp* EF004 is a compound based on Polyetherimide resin containing 20% Glass Fiber.
Tensile Strength at Break 150 MPa
21800 psi
ISO 527-1/-2
Unitika BV2120G30 PA66, 30% Glass Fiber Reinforced, Flame Retardant, Dry
Information provided by Unitika Ltd.
Tensile Strength at Break 150 MPa
21800 psi
DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® 84G33 BKB031 Nylon 66 + Nylon 6  (Unverified Data**)
33% Glass Reinforced Toughened Polyamide 66 + Polyamide 6 Zytel 84G33 BKB031 is a 33% glass reinforced toughened polyamide 66 and polyamide 6 co-melt black cube blended resin. This resin was develop..
Tensile Strength at Break 150 MPa
21800 psi
5 mm/min; ISO 527
Eurostar Staramide BG5H PA6, 25% Glass Filled, Injection Molded
BG5H is a Heat Stabilized, 25% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Tensile Strength at Break 150 MPa
21800 psi
ISO 527
Eurotec® Tecodur® PB70 GR50 BK002 CA01 PBT/PET, 50% glass fiber reinforced, heat & UV stabilized, natural
Information provided by Eurotec®
Tensile Strength at Break 150 MPa
21800 psi
ISO 527
Eurotec® Tecopet® PT70 GR30 NL100 PR PET, 30% glass fiber reinforced, high heat stabilized, natural, fast crystallization grade
Information provided by Eurotec®
Tensile Strength at Break 150 MPa
21800 psi
5mm/min; ISO 527-2/1A
Celanese CELANEX 2300 GV1/30 PBT, 30% Glass Reinforced
Chemical abbreviation according to ISO 1043-1: PBTInformation provided by Celanese
Tensile Strength at Break 150 MPa

@Temperature -40.0 °C
21800 psi

@Temperature -40.0 °F
ASTM Test
BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Conditioned)
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes..
Tensile Strength at Break 150 MPa
21800 psi
ISO 527-1/-2
BASF Ultramid® S3WG6 Balance 30% Glass Filled PA 610 (Dry)
Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. ..
Tensile Strength at Break 150 MPa
21800 psi
5mm/min; ISO 527-2/1A
Celanese ZENITE 7130 LCP, 30% Glass Reinforced
Zenite« 7130 is a 30% glass fiber reinforced liquid crystal polymer for injection molding. It has excellent impact resistance and excellent heat deflection temperature.Information provided by Celan..
Tensile Strength at Break 150 MPa
21800 psi
ISO 527-1/-2
DSM Akulon® K224-TG9 Nylon 6-45% Glass Reinforced (European and Asian Grade) (Cond)
The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Strength at Break 150 MPa
21800 psi
50%RH; ISO 527-1/-2
DuPont Performance Polymers Zytel® LM70G35HSLX BK314 Nylon 66  (Unverified Data**)
35% Glass Reinforced Heat Stabilized Laser Markable Polyamide 66 Zytel LM70G35HSLX is a 35% glass fiber reinforced heat stabilized lubricated polyamide 66 for injection molding. It is well suited fo..
Tensile Strength at Break 150 MPa
21800 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP 9X11427
LNP* THERMOCOMP* 9X11427 is a compound based on Miscellanbeous resin containing 40% specialty glass filled TP alloy. Added features of this grade include: Ultra-Stiff Toughness, Improved Impact, G..
Tensile Strength at Break 150 MPa
21800 psi
5mm/min; ISO 527-2/1A
Celanese FORTRON 6345L4 PPS, 30% Specialty
Fortron 6345L4 is 30% glass fiber/high PTFE reinforced injection molding grade. This grade, available in natural and black color, exhibits improved wear and sliding properties versus 1342L4 product...
Tensile Strength at Break 150 MPa
21800 psi
LATI Latiohm 66-04 PD01 G/25-V0CT1 PA66, 25% Glass Fiber Reinforced, Flame Retardant
Semiconductive/dissipative product based on Polyamide 66 (PA66). Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific;..