Polymer Property : Tensile Strength at Break = 21800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
Plastcom SLOVAMID 6 GF 30 HI PA6, 30% glass fibre, improved strength
FeaturesPA 6 for injection moulding, chemically strengthened with 30% glass fibre and with the content of thermoplastic kaoutchouc. Application: impacted mouldings and mouldings with high strength a..
Tensile Strength at Break 150 MPa
21800 psi
Plastcom SLOVAMID 66 GF 25 TS PA66, 25% glass fibre, thermal stability
FeaturesPA 66 for injection moulding, chemically reinforced with 25 % glass fibre, heat stabilized, suitable for high strength and high impacted mouldings. Used in automotive, engineering and electr..
Tensile Strength at Break 150 MPa
21800 psi
STN EN ISO 527-2
Plastcom SLOVAMID 66 GF 30 FRA 5 Polyamide 66, 30% Glass Fiber, Halogen Flame Retardant
FeaturesPA 66 for injection moulding, reinforced with 30% glass fiber and halogen flame retardant. Application in electrical industry: breakers, coil forms, covers, terminals. Slightly decreased f..
Tensile Strength at Break 150 MPa
21800 psi
STN EN ISO 527-2
Plastcom SLOVASTER® B GF 30 Polybutylene Terephthalate, 30% Glass Fiber
FeaturesPBT for injection moulding, chemically reinforced with 30% glass fiber. Characterized by excellent properties also at low temperatures like tensile and flexural modulus, tensile strength, a..
Tensile Strength at Break 150 MPa
21800 psi
ISO 527
Nilit FRIANYL B63 TF-GV 1530 Nylon 6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break <= 150 MPa
<= 21800 psi
ISO/R527
Polykemi AB SCANAMID 66 A33^E F45 Nylon 66, Glass Fiber Reinforced, Elastomer Modified
Information provided by Polykemi AB
Tensile Strength at Break 150 MPa
21800 psi
ISO 527
Nilit FRIANYL A63 H-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break 150 MPa
21800 psi
5mm/min; ISO 527-2/1A
Celanese VECTRA MT4310 LCP, 30% Medical Technology  (Unverified Data**)
Highest temperature capability, easiest flow. Suitable where very thin walls are required. Used for broad range of SMT applications, with minimal dimensional change. 30% glass filled.30% glass fiber..
Tensile Strength at Break 150 MPa
21800 psi
ISO 527-1/-2
DSM Akulon® S223-G8U (Cond.) 43% Glass Reinforced Nylon 66 (North America)  (discontinued **)
Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
Tensile Strength at Break 150 MPa
21800 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Lanxess Durethan® BKV 25 F30 000000 Nylon 6, Glass Fiber Reinforced, Flame Retardant
PA 6, 25% glass fibers, injection molding, flame retardantInformation provided by LANXESS.
Tensile Strength at Break 150 MPa
21800 psi
ISO 527-1/-2
Lanxess Durethan® DP 2131/20 H2.0 900051 Nylon 6, 20% Glass Fiber
PA 6, injection molding grade, 20% glass fibers, better surface resistance to alcoholic calcium chloride-solution than BKV 20 H2.0, good heat-ageing resistance and weather resistance
Tensile Strength at Break 150 MPa
21800 psi
LATI Latiohm 85-06 PD01 G/15 PES, 15% Glass Fiber Reinforced
Semiconductive/dissipative product based on Polyether Sulfone (PES). Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I..
Tensile Strength at Break 150 MPa
21800 psi
ISO 527 Type 1A
Solvay TECHNYL® A 218 V35 PA66, 35% glass fiber, Conditioned
Description: TECHNYL® A 218 V35 is a polyamide 66, reinforced with 35% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The ..
Tensile Strength at Break 150 MPa
21800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Lubricomp RCP36XXP PA 66 (Europe-Africa-Middle East)
LNP* Lubricomp* RCP36XXP is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive, Easy Molding, Internally Lu..
Tensile Strength at Break 150 MPa
21800 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP QF006 PA 6/10
LNP THERMOCOMP* QF006 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber.
Tensile Strength at Break 150 MPa
21800 psi
conditioned; ISO 527-1/-2
EMS-Grivory Grivory® AG-30 PA66-GF30
Information provided by EMS Grivory
Tensile Strength at Break 150 MPa
21800 psi
dry; ISO 527-1/-2
EMS-Grivory Grivory® HT XE 3996 PA*-GF30
Product description: Grivory XE 3996 black 9225 is a 30% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. ISO-Polymer designatio..
Tensile Strength at Break 150 MPa
21800 psi
conditioned; ISO 527-1/-2
EMS-Grivory Grivory® TSG-50 FA PA666-GF50
Information provided by EMS Grivory
Tensile Strength at Break 150 MPa
21800 psi
DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® RS 32CG20HSL BK409 Nylon 610  (Unverified Data**)
20% Carbon/Glass Reinforced Renewably Sourced Polyamide 610 Information provided by DuPont Performance Polymers
Tensile Strength at Break 150 MPa
21800 psi
5 mm/min; ISO 527
Eurostar Staramide BG5 PA6, 25% Glass Filled, Injection Molded
BG5 is a 25% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Tensile Strength at Break 150 MPa
21800 psi
5 mm/min; ISO 527
Eurostar Staramide RF005Z PA66, 25% Glass Fiber, Injection Molded
Starflam RF005Z is a 25% Glass Reinforced Polyamide 66 Injection Molding Resin (also known as Staramide RF1005E-BK82205)Information provided by Eurostar.
Tensile Strength at Break 150 MPa
21800 psi
5 mm/min; ISO 527
Eurostar Starflam RF0077P PA66/6, 35% Glass Filled, Injection Molded
Starflam RF0077P is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 66/6 Injection Molding Resin (also known as RF1007Z270EM)Information provided by Polym..
Tensile Strength at Break 150 MPa
21800 psi
ISO 527
Eurotec® Tecomid® NA40 CR10 BK111 PA6.6, 10% carbon fiber reinforced, black
Information provided by Eurotec®
Tensile Strength at Break 150 MPa

@Temperature -40.0 °C
21800 psi

@Temperature -40.0 °F
ASTM Test
BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Conditioned)
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes..
Tensile Strength at Break 150 MPa

@Temperature -40.0 °C
21800 psi

@Temperature -40.0 °F
ISO Data
BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Dry)
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes..
Tensile Strength at Break 150 MPa
21800 psi
ISO 527-2
Ascend Performance Materials Vydyne® R533T Nylon 66, Translucent, 33% Glass Filled, Conditioned (2.5% Moisture)
The Vydyne® R533T is a translucent 33% glass reinforced heat stabilized Nylon 66 product specifically designed for use in power steering reservoirs and other applications where chemical resistance,..
Tensile Strength at Break 150 MPa
21800 psi
5 [mm/min]; ISO 527-1/2
Akro-Plastic Akromid® B3 GF 20 (2470) PA 6 Dry, 20% Glass Filled
AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur..
Tensile Strength at Break 150 MPa
21800 psi
ASTM D638
LNP Thermocomp® JF-1008 Polyethersulfone, Glass Fiber Reinforcement  (discontinued **)
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Tensile Strength at Break 150 MPa

@Temperature 23.0 °C
21800 psi

@Temperature 73.4 °F
ISO 527
DuPont Performance Polymers Rynite® 530 BK503 PET  (Unverified Data**)
Rynite® 530 BK503 is a 30% glass reinforced modified polyethylene terephthalate with outstanding balance of strength, stiffness, and toughness, excellent electrical properties, surface appearance, ..
Tensile Strength at Break 150 MPa
21800 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOTUF PF00AIS PA 6
LNP THERMOTUF* PF00AIS is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.