Polymer Property : Puncture Energy = 7.38 ft-lb Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Puncture Energy	10.0 - 30.0 J @Temperature -30.0 - -30.0 °C	7.38 - 22.1 ft-lb @Temperature -22.0 - -22.0 °F	Average value: 19.0 J Grade Count:5
Overview of materials for Polycarbonate, 10% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 10% Glass Filled". Specific grades with glass content between 5% and 14% are included. Ea..
Puncture Energy	10.0 - 10.0 J @Temperature -30.0 - -30.0 °C	7.38 - 7.38 ft-lb @Temperature -22.0 - -22.0 °F	Average value: 10.0 J Grade Count:1
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E..
Puncture Energy	10.0 J @Temperature -30.0 Â°C	7.38 ft-lb @Temperature -22.0 Â°F	ISO 6603-2
Lanxess DurethanÂ® B 30 S 000000 Nylon 6 PA 6, injection molding-grade, non-reinforced, easy-flow, easy-release, rapid solidification
Puncture Energy	10.0 J @Temperature -30.0 Â°C	7.38 ft-lb @Temperature -22.0 Â°F	Conditioned; ISO 6603-2
Lanxess DurethanÂ® B 30 S 000000 Nylon 6 PA 6, injection molding-grade, non-reinforced, easy-flow, easy-release, rapid solidification
Puncture Energy	10.0 J	7.38 ft-lb	ISO 6603-2
Lanxess DurethanÂ® BKV 130 000000 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 30, even in..
Puncture Energy	10.0 J	7.38 ft-lb	ISO 6603-2
Lanxess DurethanÂ® BKV 130 H3.0 101006 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 30 H3.0, ev..
Puncture Energy	10.0 J	7.38 ft-lb	Conditioned; ISO 6603-2
Lanxess DurethanÂ® DP 2131/20 W1 901317 Nylon 6, 20% Glass Fiber PA 6, injection molding grade, 20% glass fibers, better surface finish and resistance to alcoholic calcium chloride-solution than BKV 20 H2.0, weather resistance, good heat-ageing resistance
Puncture Energy	10.0 J @Temperature -30.0 °C	7.38 ft-lb @Temperature -22.0 °F	ISO 6603-2
Covestro Makrolon® 1095 Polycarbonate, 15% Glass Filled ISO 7391-PC,MR,(,,)-09-9,GF15Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 min15 % Glass fiber reinforcedHigh viscosityEasy releaseInjection molding - Melt temperature 310 - 330 °CExtrusionAvailable ..
Puncture Energy	10.0 J @Temperature -30.0 °C	7.38 ft-lb @Temperature -22.0 °F	ISO 6603-2
Covestro Makrolon® 8315 Polycarbonate, 10% Glass Filled MVR (300 °C/1.2 kg) 6.0 cm3/10 minhigh viscosityeasy releaseinjection moldingavailable in opaque colors onlyPreprocessingMax. Water content
Puncture Energy	10.0 - 48.0 J @Temperature -40.0 - 0.000 °C	7.38 - 35.4 ft-lb @Temperature -40.0 - 32.0 °F	Average value: 23.6 J Grade Count:14
Overview of materials for Polypropylene Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene Copolymer". Each property range of values reported is minimum and maximum values of approp..