LNP Lubricomp® IBL-4416 Polyamide 6/12 Copolymer, Glass Bead Reinforced, Silicone Lubricant  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Glass Fiber Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Lubricomp® IBL-4416 Polyamide 6/12 Copolymer, Glass Bead Reinforced, Silicone Lubricant  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
Method A; ASTM D792
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Water Absorption 0.20 %
0.20 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.017 cm/cm
0.017 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.017 cm/cm
0.017 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 54.5 MPa
7900 psi
ASTM D638
Tensile Strength, Yield 54.5 MPa
7900 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ASTM D638
Elongation at Yield 3.1 %
3.1 %
ASTM D638
Tensile Modulus 3.31 GPa
480 ksi
ASTM D638
Flexural Strength 82.7 MPa
12000 psi
ASTM D790
Flexural Modulus 2.76 GPa
400 ksi
ASTM D790
Izod Impact, Notched 0.214 J/cm

@Thickness 3.18 mm
0.401 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 2.51 J/cm

@Thickness 3.18 mm
4.70 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 3.70 kJ/m²
1.76 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 16.8 kJ/m²
7.99 ft-lb/in²
ISO 180
Falling Dart Impact 3.80 J
2.80 ft-lb
ASTM D3763
Impact Test 0.970 J
0.715 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 169 °C
336 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 76.7 °C
170 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 268 - 274 °C
514 - 525 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi