LG Chemical LUCON SP9306FL sPS+MF

Category Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS)
Manufacturer LG Chemical
Trade Name LUCON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUCON SP9306FL sPS+MF.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description Injection Molding Grade, sPS+MF, Low Thermal Conductivity, Chemical Resistance, High Heat ResistanceApplication: Electrical or Electronic Parts CAS No. 9003-53-6, 65997-17-3, 68928-70-1 and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0020 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0080 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 6.0 g/10 min

@Load 2.16 kg,
Temperature 290 °C
 6.0 g/10 min

@Load 4.76 lb,
Temperature 554 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 118 MPa

@Thickness 3.20 mm
 17100 psi

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 177 MPa

@Thickness 6.40 mm
 25600 psi

@Thickness 0.252 in
 1.3mm/min; ASTM D790
Flexural Modulus 0.177 GPa

@Thickness 6.40 mm
 25.6 ksi

@Thickness 0.252 in
 1.3mm/min; ASTM D790
Izod Impact, Notched 0.686 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.29 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity 0.400 W/m-K
2.78 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 260 °C

@Thickness 6.40 mm
 500 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 220 °C

@Thickness 6.40 mm
 428 °F

@Thickness 0.252 in
 ASTM D648
UL RTI, Electrical 125 °C

@Thickness >=1.60 mm
 257 °F

@Thickness >=0.0630 in
130 °C

@Thickness >=3.00 mm
 266 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 115 °C

@Thickness >=1.60 mm
 239 °F

@Thickness >=0.0630 in
120 °C

@Thickness >=3.00 mm
 248 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 125 °C

@Thickness >=1.60 mm
 257 °F

@Thickness >=0.0630 in
130 °C

@Thickness >=3.00 mm
 266 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=1.60 mm
 V-0

@Thickness >=0.0630 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
5VA

@Thickness >=1.60 mm
 5VA

@Thickness >=0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 300 °C
500 - 572 °F
Injection Molding
Middle Barrel Temperature 270 - 320 °C
518 - 608 °F
Injection Molding
Front Barrel Temperature 275 - 320 °C
527 - 608 °F
Injection Molding
Nozzle Temperature 315 °C
599 °F
Injection Molding
Melt Temperature 315 °C
599 °F
Resin, Injection Molding
Mold Temperature 80.0 - 130 °C
176 - 266 °F
Injection Molding
Drying Temperature 120 - 140 °C
248 - 284 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 60 rpm
40 - 60 rpm
Injection Molding