Polymer Property : Tensile Strength, Yield = 118 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	118 MPa	17100 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL36 PC LNP* LUBRICOMP* DFL36 is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength, Yield	118 MPa	17100 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFL36XXP PC LNP* Lubricomp* DFL36XXP is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength, Yield	118 - 179 MPa	17100 - 26000 psi	Average value: 153 MPa Grade Count:4
Overview of materials for Nylon 66, Glass Fiber/PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Fiber/PTFE Filled". Each property range of values reported is minimum and maximum values..
Tensile Strength, Yield	118 MPa @Thickness 3.20 mm	17100 psi @Thickness 0.126 in	5mm/min; ASTM D638
LG Chemical LUCON SP9306FL sPS+MF Description Injection Molding Grade, sPS+MF, Low Thermal Conductivity, Chemical Resistance, High Heat ResistanceApplication: Electrical or Electronic Parts CAS No. 9003-53-6, 65997-17-3, 68928-70-1 ..
Tensile Strength, Yield	118 MPa	17100 psi	ASTM D638
LG Chemical LUPOS HR-2207 Heat Resistant SAN, 20% Glass Fiber Reinforced LUPOS resins are glass fiber reinforced styrene copolymers. LUPOS have improved strength, rigidity and dimensional stability. They offer excellent heat resistance, minimal mold shrinkage and have ..
Tensile Strength, Yield	118 MPa @Thickness 3.20 mm	17100 psi @Thickness 0.126 in	5mm/min; ASTM D638
LG Chemical LUPOY GP2300 PC+GF30%, Heat Resistance Description: Injection Molding, PC+GF30%, General Purpose, Heat ResistanceApplication: IT/OA, E&E Housing and Components, Automotive (Interior)CAS: 103598-77-2 and 65997-17-3Information provided by ..
Tensile Strength, Yield	118 MPa @Thickness 3.20 mm	17100 psi @Thickness 0.126 in	5mm/min; ASTM D638
LG Chemical LUPOY GN2301F PC+GF30%, Halogen Free, Flame Retardant, Heat Resistance Description: Injection Molding, PC+GF30%, Halogen Free Flame Retardant, Heat ResistanceApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 65997-17-3Information prov..
Tensile Strength, Yield	118 MPa @Thickness 3.20 mm	17100 psi @Thickness 0.126 in	5mm/min; ASTM D638
LG Chemical LUSEP SP2300 SPS+GF30%, General Purpose Feature: Injection Molding, sPS+GF30%, General PurposeApplication: Pump Units, Pick-up Lends Holder, etc.CAS No. 9003-53-6 and 65997-17-3Information provided by LG Chemical
Tensile Strength, Yield	118 MPa	17100 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP QFP36 PA6.10 (Europe-Africa-Middle East) LNP* LUBRICOMP* QFP36 is a compound based on PA6.10 resin containg Glass Fiber, PTFE, Silicone. Added features include: Internally Lubricated.
Tensile Strength, Yield	118 MPa	17100 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 LNP* LUBRICOMP* RFL33 is a compound based on Nylon 66 resin containing 15% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Tensile Strength, Yield	118 MPa	17100 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 (Asia Pacific) LNP* Lubricomp* RFL33 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength, Yield	118 MPa	17100 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP WFL34 PBT LNP LUBRICOMP* WFL34 is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
Tensile Strength, Yield	118 MPa	17100 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON DE0039 PC LNP* STAT-KON* DE0039 is a compound based on Polycarbonate resin containing 15% Carbon Fiber. Added features of this material include: Flame Retardant. Electrically Conductive.
Tensile Strength, Yield	118 MPa	17100 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP GF006 PSU (Europe-Africa-Middle East) LNP* THERMOCOMP* GF006 is a compound based on Polysulfone resin containing Glass Fiber.
Tensile Strength, Yield	118 MPa	17100 psi	5 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® GP-5300G PBT, Glass Filled Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	118 MPa	17100 psi	5 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® XP-2165M PPS Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	118 MPa	17100 psi	5 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® GP-5300G PBT, Glass Filled Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	118 MPa	17100 psi	5 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® GP-8300G MPPE, 30% Glass Filled Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	118 MPa	17100 psi	5 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® HT-8200G MPPE/PA, Glass Filled Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	118 MPa	17100 psi	5 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® XP-2165M PPS Information provided by Samsung Cheil Industries.
Tensile Strength, Yield	118 MPa	17100 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON DE0039 PC (Asia Pacific) LNP* Stat-kon* DE0039 is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Flame Retardant.
Tensile Strength, Yield	118 MPa	17100 psi	ASTM 638
PlastxWorld CEVIAN® B5526 30% GF PBT/ABS Alloy Glass fiber reinforced and flame retarded PBT/ABS alloy.Information provided by PlastxWorld Inc.
Tensile Strength, Yield	118 MPa	17100 psi	ASTM D638
Cheng Yu Plastic ML3430 PC, 30% Glass Fiber
Tensile Strength, Yield	118 MPa	17100 psi	ASTM D638
Cheng Yu Plastic N6GV10 Flame Retardant Nylon 6, 10% Glass Filled
Tensile Strength, Yield	118 MPa	17100 psi	ASTM D638, ISO R527
EPICHEM Epiter PBT GF 20 Polybutylene Terephthalate, 20% Glass Characteristics: 20% glass fibre filled
Tensile Strength, Yield	118 MPa	17100 psi	ASTM D638
Cheng Yu Plastic FR200GV25 Flame Retardant Nylon 66, 25% Glass Fiber
Tensile Strength, Yield	118 MPa	17100 psi	50mm/min; ISO 527-2
BASF Ultradur B 4300 G4 High Speed Unc. 20% Glass Filled PBT Ultradur B 4300 G4 High Speed Unc. is a high flow, fast cycling with low warpage, 20% glass filled, pigmented black, injection molding PBT for industrial parts, rigid tough and dimensional stable ap..
Tensile Strength, Yield	118 MPa	17100 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Verton RV004ESV_GY7E070 PA 66 Preliminary data for 20% long glass fiber filled, single pellet color gray, PA66This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield	118 MPa	17100 psi	ASTM 638
PlastxWorld CEVIAN® B2706 30% GF PBT/ABS Alloy Glass fiber reinforced PBT/ABS alloy.Information provided by PlastxWorld Inc.
Tensile Strength, Yield	118 MPa	17100 psi	50 mm/min; ASTM D638
Samsung Cheil Industries Infino® HM-3301GL PC, Glass Filled High Impact PC/GF material that is used for electric and electronic partsInformation provided by Samsung Cheil Industries.