- Polymer Property : Melt Flow = 6.0 g/10 min
Polymer Property : Melt Flow = 6.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products M25UVP250-01 25% Mica Reinforced Polypropylene Copolymer, UV Stabilized, Black Applications: BracketsCowl screensRigid exterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products T10P250-00 10% Talc Reinforced Polypropylene Copolymer, Natural Applications: Fan shroudsCenter consolesAir ductsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polimeri Europa Greenflex® HN 70 Ethylene Vinyl Acetate Copolymer - Compounding Greenflex HN 70 is an ethylene vinyl acetate copolymer (EVA) for compounding applications. Greenflex HN 70 is a medium fluidity grade with high tack.Main Applications: Greenflex HN 70 is recommend.. |
|||
| Melt Flow | 6.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
6.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Network Polymers NPP 1418 Description: Black Polycarbonate Polyester AlloyInformation provided by Network Polymers Inc. |
|||
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| SABIC Innovative Plastics Lexan® EX1632T PC Lexan* EX1632T polycarbonate resin is designed for use in multi-wall sheet or profile extrusion applications. It contains branched polycarbonate resin, release, and UV stabilizer. It is available .. |
|||
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| SABIC Innovative Plastics Lexan® FXM101R PC (Europe-Africa-Middle East) LEXAN FXM101R is a transparent/translucent high viscosity grade for special effects colors with a metallic-luster appearance. Color package may affect performance.This data was supplied by SABIC-IP .. |
|||
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min |
| Polimeri Europa SINKRAL C433/M3 ABS, Heat Stabilized
(discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,EG,095-08-16-15 Special low gloss grade for extrusion and calendering, with high mattness and medium impact resist.. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
|
| Lehmann & Voss LUVOCOM® 6-8503/BL Polyamide 12, unreinforced Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Dynamic stressed parts.Low waterabsorbtion.Isotropic shrinkage characteristics.Bearings, sleeve.. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| LG Chemical LUPOL HI5204S PP+MF20%, High Impact Description: Injection Molding, PP+MF20%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 26221-73-8 and 14807-96-6Information provided by LG Chemical |
|||
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Kraton® D1102 J (SBS) Liner Block Copolymer Description: Kraton D1102 J is a clear linear block copolymer based on styrene and butadiene with bound styrene of 30% mass. It is supplied from Japan in the physical form(s) identified below in the.. |
|||
| Melt Flow | 6.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
6.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Kureha KF Polymer 1000 PVDF Homopolymer KF Polymer is a fire-resistant engineering plastic which maintains the excellent performance of a fluoropolymer. It shows well-balanced molding processability similar to general-purpose resins. KF p.. |
|||
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Styrolution PS-148G Polystyrene Description: Polystyrene 148G is a high heat, easy flow general purpose polystyrene with excellent moldability, clarity and fast set-up time. It can be utilized as a coextruded gloss cap over high i.. |
|||
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® SR-0320 High Heat Resistant Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Borealis Borecene™ RM8342RC Linear Polyethylene for Rotational Molding Borecene RM8342RC is a third generation linear medium density natural polyethylene for rotational molding. Borecene RM8342RC is a special grade, which has passed many rigorous tests and can be cons.. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Borealis Borecene™ RM8402 Linear Polyethylene for Rotational Molding Borecene RM8402 is a third generation linear medium density natural polyethylene for rotational molding. The narrow molecular weight distribution imparted through metallocene catalyst technology pro.. |
|||
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Tipco Tipcolene® FPT 10 PPC - 10% Talc Reinforced Polypropylene Copolymer Compound 10% Talc Reinforced PP CopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Blue 40343/4 Concentrate Based In Polyethylene DescriptionPOLYBATCH® Blue 40343/4 is a blue color concentrate based in polyethylene. This concentrate was designed to provide color and opacity in blow molding applications. POLYBATCH® 40343/4 .. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Blue 40567 Concentrate Based In LDPE DescriptionPOLYBATCH® 40567 is a blue color concentrate based in LDPE. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATCH® 40567 is.. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Blue 40343/4 Concentrate Based In Polyethylene DescriptionPOLYBATCH® Blue 40343/4 is a blue color concentrate based in polyethylene. This concentrate was designed to provide color and opacity in blow molding applications. POLYBATCH® 40343/4 .. |
|||
| Melt Flow | 6.0 g/10 min @Load 21.6 kg, Temperature 150 °C |
6.0 g/10 min @Load 47.6 lb, Temperature 302 °F |
ISO 1133 |
| Fainplast Compounds Hax™ HF 4021/TC Flame Retardant Polyolefin Cable Compound Thermoplastic halogen free flame retardant compound based on polyolefins and mineral fillersGrade description:Improved flame retardancyInformation provided by Fainplast Compounds |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Azoty Tarnow™ TARNOFORM 300 HI4 POM High impact strength grade, high damping capacity.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
|
| BASF Polystyrol® 456 F Impact Grade Polystyrene (Europe) Heat distortion resistant, good flowing grade for parts subjected to heat.Data was collected by ISO methods and provided by BASF. |
|||
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Aclo Accutech Polypropylene Copolymer HP0335W40L Wollastonite Reinforced |
|||
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ISO 1133 |
| Ashley Polymers Ashlene® RH190ST Acetal A high impact homopolymer resin.Data provided by the manufacturer |
|||
| Melt Flow | 6.0 - 14 g/10 min @Load 21.6 kg, Temperature 232 °C |
6.0 - 14 g/10 min @Load 47.6 lb, Temperature 450 °F |
ASTM D1238 |
| Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Broad molecular weight distribution. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a.. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products M20P101-01 20% Mica Reinforced Polypropylene, Black Applications: Radiator air bafflesHVAC ductworkClose-out and filler panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Supreme Petrochem SP EXP 31 Toughened Polystyrene Characteristics Very high clarity & gloss High dart impact strength & good stiffness Good crease retention Good heat resistance High yield compared to PVC, APET Processing Extrusion Vacuum form.. |
|||
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133H |
| Total Lacqrene® 814(EU) High Impact Polystyrene
(discontinued **) LACQRENE® 814 is a PBDE free high impact, flame retardant polystyrene with excellent UV stability, rated UL 94 V0 @ 2mm and UL 94 5 VA @ 3mm.ApplicationCovers for electrical equipment, External cov.. |
|||
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min |
| Polimeri Europa SINKRAL C443 ABS, Heat Stabilized
(discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,105-08-25-20 Medium heat injection moulding grade. The availability of different industrial processes to manufa.. |
|||