Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, Dry as Molded

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon
Manufacturer Ineos ABS
Trade Name Triax®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, Dry as Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Injection molding grade with good flow and stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical damping behavior.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
Water Absorption 2.0 %
2.0 %
Saturation in water
Moisture Absorption at Equilibrium 2.0 %
2.0 %
Equilibrium at 50% RH
Water Absorption at Saturation 2.0 %
2.0 %
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
ASTM D955
Melt Flow 6.0 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 6.0 g/10 min

@Load 11.0 lb,
Temperature 500 °F
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Tensile Strength, Yield 40.0 MPa
5800 psi
Elongation at Break 140 %
140 %
ASTM D638
Elongation at Yield 3.2 %
3.2 %
Tensile Modulus 1.85 GPa
268 ksi
Flexural Yield Strength 75.0 MPa
10900 psi
at 5% strain; ASTM D790
Flexural Modulus 2.10 GPa
305 ksi
ASTM D790
Izod Impact, Notched 8.00 J/cm

@Thickness 3.20 mm
 15.0 ft-lb/in

@Thickness 0.126 in
 ASTM D256
0.800 J/cm

@Thickness 3.20 mm,
Temperature -40.0 °C
 1.50 ft-lb/in

@Thickness 0.126 in,
Temperature -40.0 °F
 ASTM D256
Charpy Impact Unnotched NB
NB
1.60 J/cm²

@Temperature -30.0 °C
 7.61 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 7.40 J/cm²
35.2 ft-lb/in²
Impact Test 14.0 J

@Thickness 3.20 mm
 10.3 ft-lb

@Thickness 0.126 in
 Instrumented Total Impact; 3.2 mm thick, 12.5 mm dart, 75 mm clamp, 6.7 m/s; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 104 µm/m-°C

@Temperature 20.0 °C
 57.8 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 118 µm/m-°C

@Temperature 20.0 °C
 65.6 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 91.0 °C
196 °F
Deflection Temperature at 1.8 MPa (264 psi) 68.0 °C
154 °F
Vicat Softening Point 102 °C
216 °F
UL RTI, Electrical 110 °C
230 °F
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL RTI, Mechanical without Impact 105 °C
221 °F
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
Dielectric Constant 3.6

@Frequency 1e+6 Hz
 3.6

@Frequency 1e+6 Hz
4.3

@Frequency 100 Hz
 4.3

@Frequency 100 Hz
Dielectric Strength 34.0 kV/mm
864 kV/in
Dissipation Factor 0.029

@Frequency 100 Hz
 0.029

@Frequency 100 Hz
0.030

@Frequency 1e+6 Hz
 0.030

@Frequency 1e+6 Hz
Arc Resistance 60 - 120 sec

@Thickness 3.18 mm
 60 - 120 sec

@Thickness 0.125 in
 UL Rating PLC 6 (60-120 sec)
Comparative Tracking Index 600 V
600 V
Hot Wire Ignition, HWI 30 - 60 sec

@Thickness 3.18 mm
 30 - 60 sec

@Thickness 0.125 in
 UL Rating PLC 2 (30-60 sec)
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.57 mm
 >= 120 arcs

@Thickness 0.0618 in
 UL Rating PLC 0 (>120 arcs)
High Voltage Arc-Tracking Rate, HVTR <= 10.0 mm/min

@Thickness 3.18 mm
 <= 0.394 in/min

@Thickness 0.125 in
 UL Rating PLC 0 (<10 mm/min.)