Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
Nylene® 404 Nylon 6 Injection molding grade. Dry as molded. Nylene 404 is a heat stabilized version of 401 which is recommended for general purpose nylon molding applications in both thin and heavy sections. In additi.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PPH T20020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
North Wood Plastics PS with 60% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C | 154 °F | ASTM D648 |
RheTech Products HP531-678UV 22% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Medium Scratch Resistant, IT3A Medium Light Stone Applications: I/P componentsInterior trimA/B/C/ PillarsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ISO 75-2 |
Polycasa LENTICULAR PETG Good ink adhesionGood receptabilityStable sheet dimensionsHigh impact strengthGood chemical resistanceEnvironmentally safeRecyclableMeets current food contact legislationDisplays Graphic Arts Advert.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
Ineos Nova 3900 General Purpose Crystal Polystyrene
(discontinued **) High flow, Good compoundingApplications: Color concentrates, Compounding, Thin wall moldingsExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the physical and o.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | |
Ineos ABS Triax® 1120 ABS + Polyamide Blend (DAM) Key Features:UnfilledPlatableHigh impact or high impact modifiedSuitable processing methods:Injection moldingFilm extrusionBlow molding |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics LNP Lubricomp FFL21 PE (Asia Pacific) LNP* Lubricomp* FFL21 is a compound based on Polyethylene resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for t.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP ML008 PP (Europe-Africa-Middle East) LNP* LUBRICOMP* ML008 is a compound based on Polypropylene resin containing PTFE. Added Features include: Internally Lubricated. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP LNP* Lubricomp* MX91206 is a compound based on Polypropylene containing proprietary fillers. Added feature of this grade is: Wear Resistant. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Valox® 364 PBT+PC Designed for outdoor telecommunications enclosure applications. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | 80x10x4mm; ISO 75-2/Af |
SYNTHOS Krasten® FB28 High Impact Polystyrene And Polyethylene Blend Polymer blend HIPS/PE. High toughness, very good tensile properties and environmental stress cracking resistance. Processed mainly by extrusion and thermoforming. Production of sheets and films, tec.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1453 Calcium Carbonate Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1453 is a long term heat aging grade of 40% calcium carbonate filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ISO 75 |
Wellman Wellamid® 22L-N Unfilled Nylon 66, Lubricated Typical Applications: Automotive components, gears, switches, bearings, pulleys, fasteners, electrical coil forms, chain-saw hand guards, cable ties, furniture hardware, small appliance housings, ae.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1453 Calcium Carbonate Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1453 is a long term heat aging grade of 40% calcium carbonate filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1453 Calcium Carbonate Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1453 is a long term heat aging grade of 40% calcium carbonate filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1453 Calcium Carbonate Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1453 is a long term heat aging grade of 40% calcium carbonate filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 892E Extrusion and Blow Molding Grade Homopolymer Polypropylene DescriptionPolyfort® FPP 892E is an extrusion and blow molding grade 20% mineral-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | DIN 53461 |
Polyram RamOfin PPH106 Polypropylene, Injection Molding polypropylene with molybdenum for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
Eastman Tenite Acetate 105E1R26033 Clear, Trsp Cellulose Acetate Plasticizer 29%. Weight loss on heating = 2.6% per ASTM D 707. Soluble matter loss = 0.4% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C | 154 °F | |
Aclo Accutech Polypropylene Homopolymer HP0339W20L1 Wollastonite Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 67.5 °C | 154 °F | ISO 75-2/A |
Cathay PA56 Renewable Engineering Polyamide, DAM Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
Ashley Polymers Ashlene® 527LDW Nylon 66 A specialized nylon with very high impact resistance.Data provided by the manufacturer |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
Ashley Polymers Ashlene® 829 Nylon 6 Basic Nylon 6, low viscosity, unlubricated.Data provided by the manufacturer |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C | 154 °F | annealed; ASTM D-648 |
Axiall 8266 Rigid PVC, Extrusion Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ISO 75 |
BASF Ultramid® C3U BK23079 PA66/6 (Dry) Ultramid C3U BK23079 is an injection molding, general purpose PA66/6, pigmented black grade with improved flame retardance. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
Beijing Chemical Industry KAIFA® HN301-G0 PA6 Resin High flame retardant, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
Toyobo Pelprene™ S-1001 Polyester TPE Key Feature: Pelprene S typePelprene™ can be processed into a wide variety of articles from ultra-small precision parts to sheets by injection, extrusion, and blow molding. The 'S' type is a block.. |