Industrial Laminates/Norplex NP631 Paper Base Laminate

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP631 Paper Base Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Hot punching grade with excellent electrical properties and low moisture absorption.Thickness Tested: 0.062", 0.125" and 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.38 g/cc
1.38 g/cc
Moisture Absorption at Equilibrium 1.0 %

@Thickness 15.7 mm
 1.0 %

@Thickness 0.620 in
Mechanical Properties Metric English Comments
Hardness, Rockwell M 105 - 125

@Thickness 1.57 mm
 105 - 125

@Thickness 0.0620 in
Tensile Strength, Yield 82.7 MPa

@Thickness 3.17 mm
 12000 psi

@Thickness 0.125 in
 CW
103 MPa

@Thickness 3.17 mm
 15000 psi

@Thickness 0.125 in
 LW
Flexural Strength 91.0 MPa

@Thickness 1.57 mm
 13200 psi

@Thickness 0.0620 in
 CW
110 MPa

@Thickness 1.57 mm
 16000 psi

@Thickness 0.0620 in
 LW
Flexural Modulus 6.21 GPa

@Thickness 1.57 mm
 900 ksi

@Thickness 0.0620 in
 CW
7.58 GPa

@Thickness 1.57 mm
 1100 ksi

@Thickness 0.0620 in
 LW
Compressive Strength 221 MPa

@Thickness 12.7 mm
 32000 psi

@Thickness 0.500 in
 Flatwise
Shear Strength 7.93 MPa

@Thickness 1.57 mm
 1150 psi

@Thickness 0.0620 in
 Perpendicular
Izod Impact, Unnotched 0.320 J/cm

@Thickness 12.7 mm
 0.600 ft-lb/in

@Thickness 0.500 in
 CW, E-48/50
0.347 J/cm

@Thickness 12.7 mm
 0.650 ft-lb/in

@Thickness 0.500 in
 LW, E-48/50
Thermal Properties Metric English Comments
CTE, linear 16.0 µm/m-°C

@Temperature 20.0 °C
 8.89 µin/in-°F

@Temperature 68.0 °F
 x-axis
CTE, linear, Transverse to Flow 20.0 µm/m-°C

@Temperature 20.0 °C
 11.1 µin/in-°F

@Temperature 68.0 °F
 y-axis
Maximum Service Temperature, Air 125 °C
257 °F
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Dielectric Constant 4.8

@Thickness 1.57 mm
 4.8

@Thickness 0.0620 in
 Permittivity, Cond D-24/23
Dielectric Strength 23.6 kV/mm

@Thickness 1.57 mm
 600 kV/in

@Thickness 0.0620 in
 D-48/50
29.5 kV/mm

@Thickness 1.57 mm
 750 kV/in

@Thickness 0.0620 in
 Condition - A
Dielectric Breakdown 15000 V

@Thickness 1.57 mm
 15000 V

@Thickness 0.0620 in
 D-48/50
60000 V

@Thickness 1.57 mm
 60000 V

@Thickness 0.0620 in
 Condition A
Dissipation Factor 0.035

@Thickness 1.57 mm
 0.035

@Thickness 0.0620 in
 Cond D-24/23
Arc Resistance 124 sec

@Thickness 3.17 mm
 124 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 200 V

@Thickness 3.17 mm
 200 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1,100 lb
0.5"