Gromax BTE65-DN001N1 Nylon 6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BTE65-DN001N1 Nylon 6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ISO 1183 |
| Moisture Absorption | 1.80 % | 1.80 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | 60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | 60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 36.3 MPa | 5260 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 285 % | 285 % | 50 mm/min; ISO 527 |
| Flexural Strength | 62.0 MPa | 8990 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 1.57 GPa | 228 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched | >= NB | >= NB | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 82.0 kJ/m² | 39.0 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 2.15 J/cm² @Temperature -30.0 °C |
10.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1A |
| 8.70 J/cm² @Temperature 23.0 °C |
41.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 285 - 300 °C | 545 - 572 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; HT (TH04) Temper; over 51 to 76 mm Thickness (UNS C17000)
- Sharadaa Ceramics ZAP 007 Smart Cast Application
- A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy
- Zig Sheng Industrial ZISAMIDE® TP4208 Nylon 6
- Loctite® 3445 1 component fusible solder filler Anisotropic Epoxy Adhesive
- Dow Corning C6-235 ELASTOMER
- 3M 9458 Adhesive Transfer Tapes with Adhesive 300
- Arlon R34381R014 0.014" (0.356 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Loctite® CHIPBONDER® 3609 Syringe Dispense
Copyright © lookpolymers.com All Rights Reserved