Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 62.0 MPa | 8990 psi | Method 1, 0.05"/min; ASTM D790 |
Proto3000 ABSi Fused Deposition Modeling Polymer Description: Stratasys ABSi is an ideal material for conceptual modeling, functional prototyping and direct digital manufacturing. Its strength is superior to standard Stratasys ABS, and the translu.. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP FARADEX KX88084 POM (Europe-Africa-Middle East) LNP* Faradex* KX88084 is a compound based on POM resin containing Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP AL004 ABS (Asia Pacific) LNP* Lubricomp* AL004 is a compound based on Acrylonitrile Butadiene Styrene resin containing Lubricants. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | <= 62.0 MPa | <= 8990 psi | ISO 178 |
Polykemi AB POLYfill PPH T4060 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP ABL12 ABS LNP* Lubricomp* ABL12 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% Glass Bead and 5% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS LNP LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Asia Pacific) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
IDI Composites 46-3 Thermoset Polyester, Molding Superior electrical performance with low pressure molding for V-O flammability in encapsulation applications.Data provided by the manufacturer. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KX06415 Acetal Copolymer LNP LUBRICOMP* KX06415 is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid Powder. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | 3-point, 2 mm/min; ISO 178 |
Styron MAGNUMâ„¢ 3416 SLG Acrylonitrile Butadiene Styrene (ABS) Resin Overview: The mass (continuous process) ABS technology of Styron ensures an ABS resin that combines excellent processability with a stable light base color providing an ideal resin for self coloring.. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KAL22M Acetal Copolymer LNP LUBRICOMP* KAL22M is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
UBE UBESTA® 3020LU1X3 Rigid Black Electronic Grade Nylon 12 Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System.. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007F Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007F is a 40% talc filled homopolymer polypropylene compound that utilizes FDA compliant raw materials.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
Unitika EX-1222 PA6, Dry High-impact nylonInformation provided by Unitika Ltd. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007 is a 40% talc filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1310 Coupled Mica Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1310 is a Coupled Mica filled homopolymer polypropylene compound for injection molding.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007 is a 40% talc filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007E is a 40% talc filled homopolymer compound for extrusion applications.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1310 Coupled Mica Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1310 is a Coupled Mica filled homopolymer polypropylene compound for injection molding.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007E is a 40% talc filled homopolymer compound for extrusion applications.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007F Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007F is a 40% talc filled homopolymer polypropylene compound that utilizes FDA compliant raw materials.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007E is a 40% talc filled homopolymer compound for extrusion applications.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007F Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007F is a 40% talc filled homopolymer polypropylene compound that utilizes FDA compliant raw materials.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007E is a 40% talc filled homopolymer compound for extrusion applications.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
Denka CL-430 Transparent Resin Polymer (MABS) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | 2 mm/min; ISO 178 |
Chi Mei Polyrex® PG-33 Polystyrene Standard grade |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
Ashley Polymers Ashlene® 833 Nylon 6 Basic Nylon 6 medium viscosity, with high residual monomer. Highly flexible and high strength, particularly suited for monofilament extrusion.Data provided by the manufacturer |
|||
Flexural Strength | <= 62.0 MPa | <= 8990 psi | ISO 178 |
Polykemi AB POLYfill PPH T5060 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON ME003S PP LNP* STAT-KON* ME003S is a compound based on Polypropylene resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Heat Stabilized. |