ExxonMobil AP3AW Polypropylene Impact Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer	Exxon Chemical
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil AP3AW Polypropylene Impact Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A UV stabilized medium impact copolymer resin designed for automotive battery cases.Availability: Asia Pacific Features:Good UV ResistanceHigh StiffnessLow WarpageMedium FlowMedium Impact ResistanceNucleated Uses: Automotive ApplicationsAutomotive Under the HoodBattery Cases Processing Method: Injection MoldingInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.900 g/cc	0.0325 lb/in³	ExxonMobil Method
Melt Flow	10 g/10 min @Load 2.16 kg, Temperature 230 °C	10 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	25.7 MPa	3730 psi	ISO 527-2/50
	27.1 MPa	3930 psi	2.0 in/min; ASTM D638
Elongation at Yield	5.6 %	5.6 %	2.0 in/min; ASTM D638
	5.7 %	5.7 %	ISO 527-2/50
Tensile Modulus	1.50 GPa	218 ksi	ISO527-2/1
Flexural Modulus	1.34 GPa	194 ksi	0.079 in/min; ISO 178
Flexural Modulus, 1% Secant	1340 MPa	194000 psi	0.05 in/min; ASTM D790A
	1520 MPa	220000 psi	0.5 in/min; ASTM D790B
Izod Impact, Notched	0.352 J/cm @Temperature -17.8 °C	0.660 ft-lb/in @Temperature 0.000 °F	ASTM D256A
	0.908 J/cm @Temperature 22.8 °C	1.70 ft-lb/in @Temperature 73.0 °F	ASTM D256A
Izod Impact, Notched (ISO)	3.36 kJ/m² @Temperature -40.0 °C	1.60 ft-lb/in² @Temperature -40.0 °F	ISO 180/1A
	4.41 kJ/m² @Temperature -17.8 °C	2.10 ft-lb/in² @Temperature 0.000 °F	ISO 180/1A
	8.82 kJ/m² @Temperature 22.8 °C	4.20 ft-lb/in² @Temperature 73.0 °F	ISO 180/1A
Charpy Impact, Notched	0.315 J/cm² @Temperature -30.0 °C	1.50 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.399 J/cm² @Temperature -20.0 °C	1.90 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eA
	0.504 J/cm² @Temperature 0.000 °C	2.40 ft-lb/in² @Temperature 32.0 °F	ISO 179/1eA
	0.987 J/cm² @Temperature 22.8 °C	4.70 ft-lb/in² @Temperature 73.0 °F	ISO 179/1eA
Gardner Impact	18.1 J @Thickness 3.17 mm, Temperature -28.9 °C	13.3 ft-lb @Thickness 0.125 in, Temperature -20.0 °F	Geometry GC; ASTM D5420

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	92.8 °C	199 °F	ISO 75-2/Bf
	99.4 °C	211 °F	Unannealed; ASTM D648
	116 °C	241 °F	Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	53.3 °C	128 °F	ISO 75-2/A