SABIC Innovative Plastics LNP Thermocomp PF0069 PA 6 (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Thermocomp PF0069 PA 6 (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* STARFLAM* PF0069 is a compound based on PA 6 resin containing Glass Fiber, Flame Retardant. Added features include; Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.64 g/cc	0.0592 lb/inÂ³	ISO 1183
Water Absorption	1.0 % @Temperature 23.0 Â°C, Time 86400 sec	1.0 % @Temperature 73.4 Â°F, Time 24.0 hour	ISO 62-1
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	150 MPa	21800 psi	5 mm/min; ISO 527
Elongation at Break	2.5 %	2.5 %	5 mm/min; ISO 527
	3.1 %	3.1 %	Flexural Strain, 2 mm/min; ISO 178
Tensile Modulus	10.0 GPa	1450 ksi	1 mm/min; ISO 527
Flexural Strength	223 MPa	32300 psi	2 mm/min; ISO 178
Flexural Yield Strength	225 MPa	32600 psi	2 mm/min; ISO 178
Flexural Modulus	9.60 GPa	1390 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	11.0 kJ/mÂ² @Temperature 23.0 Â°C	5.23 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	65.0 kJ/mÂ² @Temperature 23.0 Â°C	30.9 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	195 Â°C	383 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in	UL 94 by SABIC-IP