EMS-Grivory Grivory® BK-30 PA6-GB30
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® BK-30 PA6-GB30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 8.0 % | 8.0 % | ISO 62 |
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | dry; ISO 527-1/-2 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | |
| Elongation at Break | 5.0 % | 5.0 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 10 % | 10 % | conditioned; ISO 527-1/-2 |
| Tensile Modulus | 1.50 GPa | 218 ksi | conditioned; ISO 527-1/-2 |
| 4.30 GPa | 624 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | dry; ISO 179/1eU |
| 10.0 J/cm² | 47.6 ft-lb/in² | conditioned; ISO 179/1eU | |
| 3.00 J/cm² @Temperature 30.0 °C |
14.3 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 3.00 J/cm² @Temperature 30.0 °C |
14.3 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | dry; ISO 179/1eA |
| 1.00 J/cm² | 4.76 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.300 J/cm² @Temperature 30.0 °C |
1.43 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 0.300 J/cm² @Temperature 30.0 °C |
1.43 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 80.0 - 100 °C | 176 - 212 °F | long term; EMS |
| 160 °C | 320 °F | short term; EMS | |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | conditioned; IEC 60243-1 |
| 31.0 kV/mm | 787 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 500 V | 500 V | dry; IEC 60112 |
| 500 V | 500 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Interior | |
| Electricals & Electronics | Electrical appliances | |
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding |
Users viewing this material also viewed the following:
- Polykemi AB POLYshine PBT D221 PBT, Impact Modified
- Eastman Eastar 5445 PCTG Copolyester, Injection Molded (discontinued **)
- Ineos H03BLME Polypropylene Homopolymer
- Sylvin Technologies 9950-90 Natural PVC Molding Compound
- SABIC Innovative Plastics Valox® IQ357U PBT+PC
- Saint-Gobain CHR® 2042-10 Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- Teknor Apex Monprene® MP-2432F Thermoplastic Elastomer
- Dow DOWLEX™ 2049 Linear Low Density Polyethylene, Food Grade
- Abatron Ferrobond-LH™ Steel-Filled, Structural Adhesive Putty; High Temperature Liquid
- BASF Elastollan R 2002 25% Glass Filled TPUR
Copyright © lookpolymers.com All Rights Reserved