Dow DOWLEX™ 2101 Linear Low Density Polyethylene, Blown Film Grade

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer	Dow Chemical
Trade Name	DOWLEX™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow DOWLEX™ 2101 Linear Low Density Polyethylene, Blown Film Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DOWLEX® 2101 Polyethylene resin, a general purpose blown film extrusion resin, is an excellent choice for high speed, thin gauge film applications. It contains medium levels of both slip additive and antiblock additive. It complies with U.S. FDA Regulation 21 CFR 177.1520 (c) 3.2 (a) for food packaging applications. The regulation should be consulted for complete details.Film properties below based on a film thickness of 25 µm. Data provided by Dow Chemical.

Physical Properties	Metric	English	Comments
Density	0.924 g/cc	0.0334 lb/in³
Thickness	25.0 microns	0.984 mil
Melt Flow	1.6 g/10 min @Load 2.16 kg	1.6 g/10 min @Load 4.76 lb	Melt flow ratio I10/I2 is 8.1.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	22.1 MPa	3210 psi	Molded property
Film Tensile Strength at Yield, MD	11.7 MPa	1700 psi
Film Tensile Strength at Yield, TD	12.8 MPa	1860 psi
Tensile Strength, Yield	13.8 MPa	2000 psi	Molded property
Film Elongation at Break, MD	560 %	560 %
Film Elongation at Break, TD	700 %	700 %
Elongation at Break	800 %	800 %	Molded value
Elmendorf Tear Strength MD	230 g	230 g
Elmendorf Tear Strength TD	600 g	600 g
Elmendorf Tear Strength, MD	9.20 g/micron	234 g/mil
Elmendorf Tear Strength, TD	24.0 g/micron	610 g/mil
Dart Drop	5.20 g/micron	132 g/mil
Film Tensile Strength at Break, MD	34.5 MPa	5000 psi
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi

Optical Properties	Metric	English	Comments
Haze	13 %	13 %
Gloss	48 %	48 %	45°

Processing Properties	Metric	English	Comments
Processing Temperature	209 °C	408 °F	Film extrusion temperature