Polymer Property : Melt Flow = 1.6 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 1.6 g/10 min
1.6 g/10 min
ASTM D1238
Plaskolite Optix® CA-86 Clear General Purpose Acrylic Resin
General purpose acrylic resin, extrusion and injection molding gradeApplications: A general-purpose acrylic resin designed for high heat application. This resin offers the highest heat resistance a..
Melt Flow 1.6 g/10 min

@Load 3.80 kg,
Temperature 230 °C
1.6 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D-1238
Plaskolite Optix® CP - 86 General Purpose Acrylic Resin
OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli..
Melt Flow 1.6 g/10 min
1.6 g/10 min
ASTM D1238
Plaskolite West Optix® CA-1000 IG UC Clear High Impact Acrylic Resin
High impact acrylic resin, injection molding and extrusion gradeApplications: A premium impact acrylic resin particularly suited for medical and food uses. This resin is suited for Gamma irradiatio..
Melt Flow 1.6 g/10 min

@Load 3.80 kg,
Temperature 230 °C
1.6 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D-1238
Plaskolite West Optix® CP - 86 General Purpose Acrylic Resin
Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av..
Melt Flow 1.6 g/10 min

@Temperature 190 °C
1.6 g/10 min

@Temperature 374 °F
North Wood Plastics PS with 20% Wood Fiber
Data provided by North Wood Plastics, Inc.
Melt Flow 1.6 g/10 min
1.6 g/10 min
DuPont Fusabond® MN493D Ethylene Octene Copolymer  (discontinued **)
Typical Use: Nylon 6 toughenerNylon 6/6 toughenerComplies to FDA 21CFR 175.105Availability: North AmericaInformation provided by DuPont.
Melt Flow 1.6 g/10 min
1.6 g/10 min
Condition G
Ineos Nova 1280 High Heat Crystal Polystyrene  (discontinued **)
Good processing characteristics, Low residual monomer, Low oligomersApplications: Direct injection foam, Biaxially oriented sheet, Glazing sheetExposure to gamma radiation in the 2.02-6.06 megarad r..
Melt Flow 1.6 g/10 min
1.6 g/10 min
ExxonMobil Method
ExxonMobil LD 117.03 Blown Overwrap Film Resin  (discontinued **)
LD 117 resins are homopolymer film resins with good clarity and excellent stiffness. Film from LD 117 resins can be used in overwrap applications and push-through type packaging equipment. Film ma..
Melt Flow 1.6 g/10 min
1.6 g/10 min
ExxonMobil Method
ExxonMobil LD 117.08 Blown Overwrap Film Resin  (discontinued **)
LD 117 resins are homopolymer film resins with good clarity and excellent stiffness. Film from LD 117 resins can be used in overwrap applications and push-through type packaging equipment. Film ma..
Melt Flow 1.6 g/10 min
1.6 g/10 min
ASTM D1238
I. Stern WC-103 General Purpose Crystal Polystyrene
Features:Good Processing CharacteristicsUL Classification 94 HBExcellent Water ClarityApplicationsExtrusion FoamDisplaysInformation provided by I. Stern & Co. Inc.
Melt Flow 1.6 - 2.0 g/10 min

@Load 2.61 kg,
Temperature 190 °C
1.6 - 2.0 g/10 min

@Load 5.75 lb,
Temperature 374 °F
ASTM D1238
LG Chemical SEETEC BF415 LDPE
Characteristics: Good Processability and Excellent Optical Properties Applications: Masking filmCAS No. 9002-88-4Information provided by LG Chemical
Melt Flow 1.6 g/10 min
1.6 g/10 min
ASTM D1238
Lucky CF-920 Acrylic
May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and coloring capability.
Melt Flow 1.6 - 2.4 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.6 - 2.4 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238-00
Ipiranga Petrochem LTH 0212 LLDP
IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Melt Flow 1.6 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.6 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Borealis Borcoat™ BB700E-7032 Polypropylene Compound for Steel Pipe Coating Applications
Borcoat BB700E-7032 is a grey colored high impact polypropylene. This product is especially designed for direct extrusion of syntactic PP with high thermal insulations capacity and high compression..
Melt Flow 1.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238, ISO 1133
DuPont Surlyn® 1650SB
DuPont™ Surlyn® 1650SB is available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Slip and antiblock agents are added to ..
Melt Flow 1.6 g/10 min
1.6 g/10 min
ASTM-D1238
Westlake EB171 MDPE Medium Density Polyethylene
Westlake EF171 is a MDPE resin suggested for use in shrink packaging applications. This material has good TD shrinkage, good optical properties, excellent machinability, and toughness. This resin gr..
Melt Flow 1.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238, ISO 1133
DuPont™ Bynel® 21E787 Anhydride Modified Ethylene Acrylate
BYNEL® Series 2100 resins are anhydride modified ethylene acrylate resins. They contain a temperature stable ester which makes them functional in high temperature coextrusions. They are available i..
Melt Flow 1.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238, ISO 1133
DuPont™ Fusabond® N493 Polymer Modifier
DuPont™ Fusabond® N493 is an anhydride modified ethylene copolymer. DuPont™ Fusabond® N493 can only be used in the following applications: all polyamide blends and blends for golf balls and ble..
Melt Flow 1.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
ExxonMobil LD 117.85 Blown Overwrap Film Resin
Product Description: LD 117.85 is a homopolymer film resin with good clarity and excellent stiffness. Film made from LD 117.85 resin can be used in overwrap applications and in push-through type pac..
Melt Flow 1.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
ExxonMobil LDPE LD 117.85 Low Density Polyethylene Resin
Product Description: LD 117.85 is a homopolymer film resin with good clarity and excellent stiffness. Film made from LD 117.85 resin can be used in overwrap applications and in push-through type pac..
Melt Flow 1.6 g/10 min

@Load 2.16 kg
1.6 g/10 min

@Load 4.76 lb
Melt flow ratio I10/I2 is 10.2.
Dow AFFINITY™ SE 1400 Polyolefin Plastomer
AFFINITY® SE 1400 polyolefin plastomer is an ethylene octene resin that offers excellent performance for profile extrusion of thick tubes and good melt strength for low shear blow molding. It has e..
Melt Flow 1.6 g/10 min

@Load 2.16 kg
1.6 g/10 min

@Load 4.76 lb
Melt flow ratio I10/I2 is 8.1.
Dow DOWLEX™ 2101 Linear Low Density Polyethylene, Blown Film Grade
DOWLEX® 2101 Polyethylene resin, a general purpose blown film extrusion resin, is an excellent choice for high speed, thin gauge film applications. It contains medium levels of both slip additive a..
Melt Flow 1.6 g/10 min
1.6 g/10 min
Ashley Polymers Ashlene® ABS Resin F-216
General purpose high impact resin.Data provided by the manufacturer
Melt Flow 1.6 g/10 min

@Load 3.80 kg,
Temperature 230 °C
1.6 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Arkema Group Solarkote® A200 Acrylic
Superior UV protection and weatherability, ASTM Classification PMMA 0233V1Information provided by Arkema Group
Melt Flow 1.6 g/10 min

@Load 3.80 kg,
Temperature 230 °C
1.6 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D-1238
Plaskolite Optix® CP - 86 UVA General Purpose Acrylic Resin
OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli..
Melt Flow 1.6 g/10 min
1.6 g/10 min
Condition G
Ineos Nova 1204 High Heat Crystal Polystyrene
Good processing characteristics, High tensile strength and modulus, Excellent clarity, USP Class VIApplications: Direct injection foam, Biaxially oriented sheet, Glazing sheetExposure to gamma radia..