- Polymer Property : Tensile Strength, Yield = 2000 psi
Polymer Property : Tensile Strength, Yield = 2000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | Mixed 1:1; TM R050-36 |
| Resinlab® EP1215 Clear Unfilled Epoxy Structural Adhesive Resinlab™ EP1215 Clear is a two part unfilled epoxy structural adhesive designed for bonding applications requiring high strength and good impact resistance. It cures completely at room temperature.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable JA306BA Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable W1250L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable W2301 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ASTM D638 |
| S&E Specialty Polymers TufFill NH™ GTPO8290-36 TPO Application: A 105°C rated, Flexible, TPO based, Zero Halogen compound, exhibiting excellent processing characteristics with superior physical and low temperature propertiesInformation provided by .. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible R7542X Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength, Yield | 13.8 MPa @Thickness 3.17 mm |
2000 psi @Thickness 0.125 in |
2"/min speed; ASTM D638 |
| PolyOne Maxxam® FR PE 125 Low Density Polyethylene, Wire and Cable
(discontinued **) Data provided by PolyOne. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | |
| Saint-Gobain Rulon® E Grade Bearing/Seal PTFE
(discontinued **) Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of friction, and .. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | 20"/min; ASTM D638 |
| LyondellBasell Petrothene® GA564189 Linear Low Density Polyethylene, Injection Molding Grade PETROTHENE GA564189 exhibits good stiffness and low temperature toughness. Typical applications include trash cans, industrial containers, housewares and toys. Regulatory Status: GA564189 meets the .. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ASTM D412-97 |
| Saint-Gobain Tygon® SE-200 Inert Tubing Formulation Description: Tygon® SE-200: Without sacrificing the flexibility, glass-like clarity or outstanding bend radius for which Tygon® tubing is known, Tygon® Inert Tubing can handle many applic.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ASTM D412 |
| Teknor Apex Flexalloy® 3501-60-NT Polyvinyl Chloride Elastomer Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Features: Ultra High MW, Ethylene Oxide SterilizableForms-PelletsProcessing-Extrusion, Injection MoldingAppe.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | machine direction; ASTM D882 |
| A. Schulman CP80-01 Linear Low-Density Polyethylene DescriptionCP 880-01 natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties.ApplicationCP 880-01 meets FDA Regulation 21 CFR 177.1250(c) 3.1 and 3.2.In.. |
|||
| Tensile Strength, Yield | >= 13.8 MPa | >= 2000 psi | Heat Aging (7 days at 121°C); ASTM D638 |
| Borealis Visico™ ME4425/LE4462 Scorch Retardant Silane Crosslinkable MDPE Track Resistant Cable Insulation Visico ME4425/LE4462 is a combination of LE4425, a Medium Density Visico base resin and a masterbatch, LE4462, which contains catalyst, carbon black, UV stabilizers and antioxidants. The LE4462 mas.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | machine direction; ASTM D882 |
| A. Schulman CP80-01 Linear Low-Density Polyethylene DescriptionCP 880-01 natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties.ApplicationCP 880-01 meets FDA Regulation 21 CFR 177.1250(c) 3.1 and 3.2.In.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | machine direction; ASTM D882 |
| A. Schulman CP80-01 Linear Low-Density Polyethylene DescriptionCP 880-01 natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties.ApplicationCP 880-01 meets FDA Regulation 21 CFR 177.1250(c) 3.1 and 3.2.In.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | machine direction; ASTM D882 |
| A. Schulman CP80-01 Linear Low-Density Polyethylene DescriptionCP 880-01 natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties.ApplicationCP 880-01 meets FDA Regulation 21 CFR 177.1250(c) 3.1 and 3.2.In.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ISO 527-1/2 |
| CTC X-PRO TF 1040 GP Polypropylene Homopolymer, 40% Talc Filled X-PRO TF 1040 GP is a 40% talc reinforced polypropylene homopolymer and made of 98% recycled content. It has applications in: automotive, industrial, construction, consumer and lawn & garden produc.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ISO 527-1/2 |
| CTC X-PRO TF 2104 GP Recycled Polypropylene Homopolymer, 20% Talc Filled X-PRO TF 2104 GP is a 20% talc reinforced polypropylene homopolymer made of 98% recycled content. It has applications in: automotive, industrial, construction, consumer and lawn & garden products.D.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ASTM D638 |
| ExxonMobil LDPE LD 157CW Wire & Cable Low Density Polyethylene Resin Product Description: LD 157CW is a medium density LDPE recommended for the production of Low Voltage power cable insulation, using the on-step silane cross0linking technology. The grade contains a h.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ASTM D-638 |
| Axiall 8710 Moldings & Extrusions Flexible PVC Low gravity extrusion compound with excellent low temperature properties. Designed for use in weatherstrips and flexible gaskets. Excellent for co-extrusion with rigid PVC.Information provided by .. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ASTM D-638 |
| Axiall 8742 Moldings & Extrusions Flexible PVC General purpose extrusion compound recommended for use in weatherstrips, screen splines and other extruded shapes and profiles.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporat.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ASTM D-638 |
| Axiall 10750 Wire & Cable Flexible PVC General purpose 75C jacket compound with good low temperature properties.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ASTM D-638 |
| Axiall 12791 Wire & Cable Flexible PVC General purpose, 75°C rated non-lead stabilized jacket compound with good low temperature properties and 720 hour sunlight resistance.Information provided by Georgia GulfGeorgia Gulf became Axiall .. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Atomite Whiting Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | ASTM D638 |
| A. Schulman POLYTROPE™ TPP 615 Olefinic Elastomer DescriptionPolytrope TPP 615 is an olefinic elastomer developed to exhibit very low thermal expansion, high DOI on painted parts with good low temperature impact properties. ApplicationTPP 615 is de.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | TM R050-36 |
| Resinlab® EP965LVLX Clear Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP965LVLX Clear is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It cures at room temperature to a tough, semi-rigid polymer. It has .. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | |
| Resinlab® UR1049 MDI Based Rigid Polyurethane Foam System Resinlab™ UR 1049 is a, two component, water blown, 4 lb per cubic foot, MDI based rigid polyurethane foam system. It is designed to cure completely at room temperature. Being of a closed cell stru.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Atomite Whiting Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | at 100%; ASTM D412 |
| EG60D Polyurethane-based Biomedical Elastomer |
|||