Borealis MS64T20 Polypropylene Compound, Mineral Filled

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Borealis
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis MS64T20 Polypropylene Compound, Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MS64T20 is a 20% mineral filled polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties and is easy to process. Applications: automotive parts including cowl vent grilles, automotive interior applications, and automotive exterior applications.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Linear Mold Shrinkage 0.011 cm/cm
0.011 in/in
Borealis Method; average process
Melt Flow 22.5 g/10 min

@Load 2.16 kg,
Temperature 230 °C
22.5 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 93.0 MPa
13500 psi
132N/10s; ISO 2039
Tensile Strength, Yield 32.0 MPa
4640 psi
50mm/min; ISO 527-2
Elongation at Break 13 %
13 %
50mm/min; ISO 527-2
Elongation at Yield 5.0 %
5.0 %
50mm/min; ISO 527-2
Tensile Modulus 3.10 GPa
450 ksi
1mm/min; ISO 527-2
Flexural Strength 56.0 MPa
8120 psi
ISO 178
Flexural Modulus 3.20 GPa
464 ksi
2mm/min; ISO 178
Izod Impact, Notched (ISO) 2.10 kJ/m²

@Temperature -20.0 °C
0.999 ft-lb/in²

@Temperature -4.00 °F
ISO 180/1A
4.00 kJ/m²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 1.50 J/cm²

@Temperature -20.0 °C
7.14 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
3.80 J/cm²

@Temperature 23.0 °C
18.1 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.0600 J/cm²

@Temperature -30.0 °C
0.286 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.120 J/cm²

@Temperature -20.0 °C
0.571 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
0.250 J/cm²

@Temperature 23.0 °C
1.19 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 56.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
31.1 µin/in-°F

@Temperature -22.0 - 176 °F
Borealis Method
Deflection Temperature at 0.46 MPa (66 psi) 120 °C
248 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 66.0 °C
151 °F
ISO 75-2
Vicat Softening Point 97.0 °C

@Load 5.10 kg
207 °F

@Load 11.2 lb
ISO 306
154 °C

@Load 1.02 kg
309 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 - 260 °C
428 - 500 °F
mass temperature
Feed Temperature 40.0 - 80.0 °C
104 - 176 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec
3.94 - 7.87 in/sec
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Descriptive Properties Value Comments
Back Pressure low to medium
Fogging (mg) 0.5
100°C, 16h; DIN 75201
Screw Speed low to medium