Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 32.0 - 36.0 MPa | 4640 - 5220 psi | |
Reliance Industries Polypropylene Homopolymer Typical properties of Reliance - Repol Polypropylene gradesInformation provided by Reliance Industries |
|||
Tensile Strength, Yield | 32.0 - 237 MPa | 4640 - 34400 psi | Average value: 101 MPa Grade Count:51 |
Overview of materials for Nylon 610 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610". Each property range of values reported is minimum and maximum values of appropriate MatWeb e.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-1, 2 |
LyondellBasell Moplen HP400L Polypropylene Homopolymer Description: All ingredients in HP400L meet the chemical registration requirements of TSCA (U.S.) and DSL (Canada). Uses: Toys, containers, lids, medical applications, closure capsInformation provid.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
Flint Hills P5L2Z-038 Random Copolymer Polypropylene Random copolymer, USP Class VI certified, and FDA compliant.Features: Hydrotalcite.Applications: Injection molding: extrusion blow molding and hot fill applications.Former Huntsman polypropylene pro.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638-02 |
Ipiranga Petrochem GF 4960 HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce .. |
|||
Tensile Strength, Yield | 32.0 MPa @Strain 0.200 %, Temperature 1093 °C |
4640 psi @Strain 0.200 %, Temperature 1999 °F |
|
Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D 638 |
LyondellBasell Hifaxâ„¢ AA36H Polypropylene Homopolymer Description: Hifaxâ„¢ AA36H conventional melt flow, 1,400 MPa flexural modulus, UL 94 V-2 flame retardant polypropylene homopolymer resin has an excellent combination of properties and processabi.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP ML004LS PP LNP* LUBRICOMP* ML004LS is a compound based on Polypropylene resin containing 20% PTFE. Added features of this matLNP* Lubricomp* ML004LS is a compound based on Polypropylene resin containing PTFE... |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON MX01767C PP LNP* STAT-KON* MX01767C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Asia Pacific) LNP* Stat-loy* A30009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant. Added features of this material include: Antistat, Flame Retardant. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Asia Pacific) LNP* Stat-loy* A3000T is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50mm/min; ISO 527-2 |
Borealis PS65T20 Polypropylene Compound, Mineral Filled PS65T20 is a 20% mineral filled polypropylene compound intended for injection and back injection molding. This material has excellent balanced mechanical properties and high melt flow rate. Applic.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | at 50 mm/min; ASTM D638 |
A. Schulman PP 1248-01 Polypropylene High-Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1248-01 is a high-flow homopolymer polypropylene nucleated and anti static designed for the high speed molding of thin-walled, multi-cavity parts. ApplicationTypical appl.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2 |
Total PPH 10060 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 10060 homopolymer. PPH 10060 is characterized by high fluidity and is particularly suitable for injection molding applications. The material provides a good balance betwe.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2 |
Total PPH 7062 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 7062 is an antistatic homopolymer.ApplicationATOFINA Polypropylene PPH 7062 is intended for injection molding applications of boxes, closures and household articles. Inform.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2 |
Total PPH 7069 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 7069 is homopolymer.ApplicationATOFINA Polypropylene PPH 7069 is characterized by medium fluidity for extrusion of continuous filament (CF) and bulk continuous filament (BC.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ASTM D638 |
A. Schulman PP 1621 Polypropylene Low Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1621 is a low flow homopolymer polypropylene primarily used for sheet strapping and profile extrusion applications.ApplicationPP 1621 meets FDA Regulation 21 CFR 177.1520.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50mm/min; ISO 527-2 |
Borealis MS64T20 Polypropylene Compound, Mineral Filled MS64T20 is a 20% mineral filled polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties and is easy to process. Applications: automotive p.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2 |
Total PS CPDS 853 Flame Retardant Polystyrene POLYSTYRENE (PS) COMPOUND (CPDS) 853 is a high impact, high stiffness halogen free flame retardant polystyrene.Main Characteristics:Bromine and Chlorine free,UL94 V2 @ 1.6 mm with very low combustio.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ASTM D638 |
A. Schulman PP 1621 Polypropylene Low Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1621 is a low flow homopolymer polypropylene primarily used for sheet strapping and profile extrusion applications.ApplicationPP 1621 meets FDA Regulation 21 CFR 177.1520.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
Eurostar Starpylen MK001AS PP, Mineral Filled, Injection Molding Starpylen MK001AS is a Mineral Filled Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO R527 |
Arkema Group Orgalloy® LE 60 LM Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339C10L1 Calcium Reinforced |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527 |
Azoty Tarnow™ TARFLEN SG-1 PTFE Free-Flowing suspension powder for automated compression molding of complicated shapes and isostatic pressing.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
Carmel Olefins CAPILENE® T 50 Polypropylene Homopolymer CAPILENE® T 50 is a high melt flow rate homopolymer for injection molding characterized by good flow properties combined with good stiffness. APPLICATIONS CAPILENE ® T 50 is recommended for in.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM-D638 |
Braskem CP 202XP HECO Polypropylene Heterophasic Copolymer CP 202XP is a high melt flow rate heterophasic copolymer designed to achieve parts with high stiffness and impact strength resistance, low warpage, and excellent surface appearance. Its applications.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer HP0334W30L Wollastonite Reinforced |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 572-2 |
Total Lacqrene® 852 High Impact Polystyrene
(discontinued **) LACQRENE® 852 is a flame retardant, high impact polystyrene, halogen free, with excellent thermal stability.ApplicationCopier, Fax, Printers, Television, decoders, Hi-FiInformation provided provide.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® RS 3261THSL BK041A Nylon 610
(Unverified Data**) Toughened Renewably Sourced Polyamide 610 Developed for Injection Molding Zytel RS 3261THSL BK041A is a renewably sourced polyamide 610 resin containing a minimum of 47% renewably sourced ingredient.. |
|||
Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
BP Amoco Acclear® 8649X Random Copolymer Polypropylene, High Clarity Grade
(discontinued **) Developmental Grade. Suggested fabrication methods: Injection molding; Stretch blow moldingFeatures: Ultra high clarity, Low taste/odor, Excellent processabilityTypical applications: High clarity c.. |