Polymer Property : Flexural Strength = 8120 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	56.0 MPa	8120 psi
Plastcom SLOVALEN PH 71 T 40 PP, 40% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 40% microground, floated, chemically modified talc. General application in all industry branches - packing material, garden..
Flexural Strength	<= 56.0 MPa	<= 8120 psi	ISO 178
Polykemi AB POLYfill PPHC T20050 Polypropylene, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	56.0 MPa	8120 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP AI001XXH ABS LNP* Lubricomp* AI001XXH is a compound based on ABS containing 2% Silicone. Characteristics of this grade are: Healthcare and Internally Lubricated.
Flexural Strength	56.0 MPa	8120 psi	ISO 178
Nilit FRIANYL C73 M-HS3005 Nylon 6.6/6 for injection molding, 30% mineral filled Nylon 6.6/6 for injection molding, medium viscosity, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	56.0 MPa	8120 psi	ASTM D790
FiberfilÂ® J-68/20/E/SD/HM Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled, with static dissipation Information provided by FIBERFIL Engineered Plastics
Flexural Strength	56.0 MPa	8120 psi	2mm/min; ASTM D790
Kingfa FW-650 Flame Retardant ABS Features:Weather resistanceSuper high impact resistanceApplications:Injection moldingSwitchSocketInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Flexural Strength	>= 56.0 MPa	>= 8120 psi
MarkeTech Repton 214 Aluminum Oxide Brand 214 features: High porosity and purity.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even wh..
Flexural Strength	56.0 MPa	8120 psi	ASTM D790
FiberfilÂ® J-68/20/E/SD Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled, with static dissipation Information provided by FIBERFIL Engineered Plastics
Flexural Strength	56.0 MPa	8120 psi	ASTM D790
SABIC Innovative Plastics NORYL TCN8222 PPE+HIPS (Asia Pacific) PPE/HIPS unfilled 80C FR-V2
Flexural Strength	56.0 MPa	8120 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP OL003A PPS - Branched LNP* LUBRICOMP* OL003A is a compound based on PPS - Branched resin containing 15% PTFE. Added features of this grade are: Wear Resistant.
Flexural Strength	56.0 MPa	8120 psi	ISO 178
Solvay TECHNYLÂ® C 52G3 MZ25 PA6, Conditioned Description: Flame retardant polyamide PA6 reinforced with mineral filler, for injection molding.Available in: Asia Pacific, Europe, Latin America and North America Product Applications: This phosph..
Flexural Strength	56.0 MPa	8120 psi	ISO Data
Styrolution TerluranÂ® HI-10 ABS Terluran HI-10 is an injection molding and extrusion grade of ABS with very high toughness and medium flow.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Flexural Strength	56.0 MPa	8120 psi	ISO 178
Styrolution TerluranÂ® SP-6 ABS Description: High impact grade, suitable for extrusion.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
Flexural Strength	56.0 MPa	8120 psi	ASTM D790
Plenco 7487 Phenolic, Granular, Transfer Molded PLENCO 07487 is a rubber modified organic reinforced phenolic molding compound offering improved mechanical strength and lower modulus. Plenco 07487 is available in black.Information supplied by Ple..
Flexural Strength	56.0 MPa	8120 psi	ISO 178
Borealis MS64T20 Polypropylene Compound, Mineral Filled MS64T20 is a 20% mineral filled polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties and is easy to process. Applications: automotive p..
Flexural Strength	56.0 MPa	8120 psi	2 mm/min; ISO 178
Chi Mei Polylac® PA-758 ABS - Transparent Transparent
Flexural Strength	56.0 MPa	8120 psi	23°C, 50% RH; ASTM D790
Asahi Kasei Xyron® 100V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei
Flexural Strength	56.0 MPa	8120 psi	23°C, 50% RH; ASTM D790
Asahi Kasei Xyron® 200H Modified Polyphenylene Ether Heat ResistantInformation provided by Asahi Kasei
Flexural Strength	56.0 MPa	8120 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 121 Polypropylene, Glass Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.11% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	56.0 MPa	8120 psi	ASTM D790
Fiberfil® J-68/20/E Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics