BASF Ultramid® B3GM35 BKQ642 23220 15/25% Glass/Mineral Filled PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3GM35 BKQ642 23220 15/25% Glass/Mineral Filled PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3GM35 BKQ642 23220 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 2.2 % | 2.2 % | 24 hour; ISO Test |
| 6.6 % | 6.6 % | ISO 62 | |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 160 cm³/g | 160 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | 5mm/min; ISO 527 |
| 2.7 % | 2.7 % | 0.2 in/min; ASTM Test | |
| Tensile Modulus | 8.00 GPa | 1160 ksi | ASTM Test |
| 9.00 GPa | 1310 ksi | 1mm/min; ISO 527 | |
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C |
0.749 ft-lb/in @Temperature -40.0 °F |
ASTM Test |
| 0.530 J/cm @Thickness 3.17 mm |
0.993 ft-lb/in @Thickness 0.125 in |
ASTM Test | |
| Charpy Impact, Notched | 0.390 J/cm² | 1.86 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| 220 °C | 428 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75 |
| 215 °C | 419 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | ISO 75 |
| 200 °C | 392 °F | ASTM Test |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK23220 | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- PolyOne OnForce™ LFT PP-50LGF/001 UV Black Polypropylene Homopolymer (PP Homopolymer)
- ExxonMobil Santoprene® 261-87 Thermoplastic Elastomer (discontinued **)
- Plastcom SLOVAMID 6 HI/1 TLS PA6, improved strength
- Covestro Bayblend® KU2-1500 Polycarbonate + ABS Blend, Extrusion/Blow-Molding (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK
- SABIC Innovative Plastics NORYL GFN3V PPE+HIPS (Europe-Africa-Middle East)
- CLAL-MSX CUPROROR® TL1 1/4 hard, Copper Alloy
- CP-Polymer-Technik Wellamid® 6000 CF 18 HWCP 18% Carbon Fiber Nylon 6, Heat Stabilized, Dry
- BCC Products BE 290 Epoxy Laminating System
Copyright © lookpolymers.com All Rights Reserved