Polymer Property : Tensile Modulus = 1310 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	9.00 GPa	1310 ksi	50 mm/min; ASTM D638
Ovation Polymers Opnyl OP66GF43 Nylon 66, As Conditioned Nylon 66-Glass reinforced(43%), high tensile strength, stiffness and HDT.Information provided by Ovation Polymers
Tensile Modulus	9.00 GPa	1310 ksi	ASTM D638
Premix Premi-Glas® 1201-15 Polyester SMC Premi-Glas® 1201-15 is a 15% glass reinforced thermoset Sheet Molding Compound designed for sinks, shower stall bases and wall applications. Key features and benefits are:Supports ANSI 124.2 and CS..
Tensile Modulus	9.00 GPa	1310 ksi	ASTM D638
Premix Premi-Glas® 2200-15 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2200-15 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal ..
Tensile Modulus	9.00 GPa	1310 ksi	ASTM D638
Premix Premi-Glas® 2203-15 CR-SX-HT Fiberglass Reinforced Thermoset SMC Premi-Glas® 2203-15 CR-SX-HT is a fiberglass reinforced thermoset sheet molding compound for electrical and flame retardant applications.Key features and benefits are:Enhanced product for higher UL..
Tensile Modulus	9.00 GPa	1310 ksi	ISO 527-1,2
Qualchem Danamid FGFHUV-30 Polyamide 6, 30% Glass Fiber Reinforced with glass fiber. Heat and UV stabilized, for long-lasting use at 120-140°C, resistant to artificial light.Information provided by Qualchem Zrt.
Tensile Modulus	9.00 GPa	1310 ksi	ISO 527
Premix Thermoplastics PRE-ELEC® 12-031 (discontinued **) PRE-ELEC 12-031 is a conductive thermoplastic compound based on a polyacetal copolymer with 10% carbon fiber. PRE-ELEC 12-031 exhibits excellent mechanical properties and electrical conductivity. Te..
Tensile Modulus	9.00 GPa	1310 ksi	ASTM D638
Loxim 140 01V0 Polycarbonate, 40% Glass Filled, Flame Retardant Information provided by Loxim Industries
Tensile Modulus	9.00 GPa	1310 ksi	ISO 527-1/-2
Lanxess PocanÂ® DP 4035 000000 PBT + PET, 30% Glass Fiber PBT+PET, 30% glass fibers, injection molding, halogen free flame retardant
Tensile Modulus	9.00 GPa	1310 ksi	ISO 527
Solvay TECHNYLÂ® A 718 V30 PA66, 30% glass fiber, DRY Description: TECHNYL A 718 V30 is a polyamide 66 reinforced with glass fiber and thermal stabilized for injection moldingColors: it is sailed on natural and black colorAvailable in: Latin AmericaMai..
Tensile Modulus	9.00 GPa	1310 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WFP36 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Silicone.
Tensile Modulus	9.00 GPa	1310 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® 5031 PBT (Europe-Africa-Middle East) VALOX 5031 is a 30% glass reinforced PBT+PC blend with low warpage characteristics. Applications: appliance handles, automotive doorhandles. This grade is a 508 with reduced warpage.
Tensile Modulus	9.00 GPa	1310 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® 830F PBT+PET PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications
Tensile Modulus	9.03 GPa	1310 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DX06412H PC LNP* THERMOCOMP* DX06412H is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Tensile Modulus	9.00 GPa	1310 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics NORYL NH8006 PPE+HIPS (Asia Pacific) Noryl* NH8006 resin is a 30% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve a UL94 V0 flame rating (color specific) while offering an exceptio..
Tensile Modulus	9.00 GPa	1310 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics NORYL GTX GTX230 PPE+PA66 (Europe-Africa-Middle East)
Tensile Modulus	9.00 GPa	1310 ksi	ISO 527-2
Borealis Xmod™ GB305HP High Performance 35% Glass Fiber Reinforced Xmod GB305HP is reinforced with 35% chemically coupled glass fibers and based on a specific Polymer matrix material that is bringing excellent mechanical properties (biaxial impact behavior) as well..
Tensile Modulus	9.00 GPa	1310 ksi	1 mm/min; ISO 527
Eurostar Staramide RFC16 PA66/6, Glass/Carbon Fiber Filled, Injection Molded RFC16 is a Glass Fiber and Carbon Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as STAR C PA66 C 303VY Z3)Information provided by Eurostar.
Tensile Modulus	9.00 GPa	1310 ksi	ISO 527
Eurotec® Tecomid® NB40 GR30 NL MB PA6, 30% glass fiber reinforced, impact modified, heat stabilized, natural Information provided by Eurotec®
Tensile Modulus	9.00 GPa	1310 ksi	ISO 527
Eurotec® Tecomid® NA40 CR10 BK111 PA6.6, 10% carbon fiber reinforced, black Information provided by Eurotec®
Tensile Modulus	9.00 GPa	1310 ksi
BASF Luranyl® KR 2403 G6 Polyphenylene Ether + Styrene-Butadiene Blend, 30% Glass Fiber Reinforced General-purpose grade with 30% glass fiber for parts requiring especially good resistance to heat deformation.Applications: parts for hot-water contact, pump housings, fan blades.Data was collected ..
Tensile Modulus	9.00 GPa	1310 ksi	ISO 527-2
BASF Ultramid® T 4381 LDS 10/25% Glass/Mineral Filled PA6/6T (Dry) Description: Ultramid® T 4381 LDS is a semi-crystalline, partially aromatic high temperature polyamide (PA6/6T) for laser direct structuring (LPKFLDS®). As the material is reinforced with 10% fibe..
Tensile Modulus	9.00 GPa	1310 ksi	dry; ISO 527
Azoty Tarnow™ Tarnamid® T-27 GF30 Polyamide 6 - Glass Fiber Reinforced 30% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High..
Tensile Modulus	9.00 GPa	1310 ksi	dry; ISO 527-1/-2
DSM Stanyl® TC502 PA46 Thermal conductive material
Tensile Modulus	9.06 GPa	1310 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PH0800A PA 6 LNP* THERMOCOMP* PH0800A is a compound based on Nylon 6 resin. Added feature of this material is: High Specific Gravity.