Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ASTM D638 |
Shell Carilon® DP R1130 Polyketone, 30% Glass Fiber Reinforced
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON® Thermoplastic Polymer DP R1130 is a 30 percent glass fiber reinforced compound based on a developmental e.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527 |
LATI LAPEX A G/30 30% Glass Fiber Reinforced Polyethersulfone (PES) (UL94 V-0)
(Unverified Data**) Description: Lapex A compounds are polyethersulfone (PES) products. They are high temperature compounds offering an interesting combination of properties. Lapex A provides outstanding thermal resist.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527 |
LATI LAXTAR G/30 30% Glass Reinforced LCP
(discontinued **) Description: Laxtar products are liquid crystal polymers (LCP). They offer exceptional performance together with increasing cost-effectiveness. Due to the outstanding fluidity at high shear rates LC.. |
|||
Tensile Strength, Ultimate | 130 - 130 MPa @Temperature 130 - 175 °C |
18900 - 18900 psi @Temperature 266 - 347 °F |
Average value: 147 MPa Grade Count:1 |
Overview of materials for Nylon 66, 60% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. .. |
|||
Tensile Strength, Ultimate | 130 - 130 MPa @Time 1.80e+7 - 7.20e+7 sec |
18900 - 18900 psi @Time 5000 - 20000 hour |
Average value: 147 MPa Grade Count:1 |
Overview of materials for Nylon 66, 60% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. .. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527 |
Solvay Specialty Polymers Ryton® R-7-120BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-7-120BL is an advanced glass/mineral filled polyphenylene sulfide compound developed to provide good weldline strength and low maintenance molding using.. |
|||
Tensile Strength, Ultimate | 130 MPa @Temperature 22.0 °C |
18900 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 1400 Unsaturated Polyester UP SMC 1400 is a special SMC being used in the environment of a combustion engine. The glass level has been selected to combine good mouldability with good stiffness and strength properties. The produc.. |
|||
Tensile Strength, Ultimate | 130 MPa @Temperature 1095 °C |
18900 psi @Temperature 2003 °F |
|
Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1, 2 |
Polyplastics FR-PET® CN9030 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose Information provided by PolyPlastics. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ASTM D638 |
Toyobo Vylopet® EMC130-01 Glass Reinforced Polyester, Standard Grade Key Feature: Flame retardant V-0 UL-94 classApplications: General and high rigidity componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric stren.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1/-2 |
DSM Arnite® TV4 261 SF PBT-GF30 FR(17) 30% Glass Reinforced, Flame Retardant, High Flow |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1/-2 |
DSM Arnite® TV4 461 (PBT+PET)-GF30 30% Glass Reinforced |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | cond; ISO 527-1/-2 |
DSM EcoPaXX® Q-X07209 PA410-I-GF40 % Glass Reinforced, Impact Modified |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1013G15 1 NA PA6-GF15 15% Glass Reinforced, Injection Molding |
|||
Tensile Strength, Ultimate | 130 MPa @Temperature 120 °C |
18900 psi @Temperature 248 °F |
ISO 527-1/-2 |
DSM Stanyl® TE200F8 PA46-GF40 40% Glass Reinforced, Heat Stabilized, for E&E applications |
|||
Tensile Strength, Ultimate | 130 MPa @Temperature 120 °C |
18900 psi @Temperature 248 °F |
ISO 527-1/-2 |
DSM Stanyl® TW272B6 (PA46+PTFE)-CF30 30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
BASF Petra® 130 FR 30% Glass Filled PET Petra 130 FR is a 30% glass fiber reinforced, flame retardant injection molding polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. It is also avail.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Dry) Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes.. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO R527 |
Arkema Group Orgalloy® RS 6030 Polyamide 6 Alloy 30% Glass Fiber reinforced Polyamide Alloy, Rigid grade, Nylon 6 basedMolding of Engineering PartsInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4300 G6 BKQ16 15007 PBT |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4406 G4 BKQ113 7110 20% Glass Filled PBT Ultradur B 4406 G4 BKQ113 7110 is an UL V0 injection molding, pigmented black, PBT grade with 20% glass fiber reinforcement. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
BASF Ultramid® B3GM35 BKQ642 23220 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid B3GM35 BKQ642 23220 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade. |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1/-2 |
DSM Arnite® TV4 261 KL PBT-GF30 30% Glass Reinforced, Light Stabilized |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1/-2 |
DSM Arnite® TV4 264 SN PBT-GF30 FR(17) 30% Glass Reinforced, Flame Retardant |
|||
Tensile Strength, Ultimate | 130 MPa | 18900 psi | ASTM D638 |
Chevron Phillips Ryton® R-7 02 Polyphenylene Sulfide Compound
(discontinued **) Black Polyphenylene Sulfide CompoundRyton® R-7 02 is polyphenylene sulfide compounded with glass fibers and mineral fibers to produce an injection moldable high temperature engineering compound wit.. |