Azoty Tarnow™ Tarnamid® T-30 MS Polyamide 6 - Natural

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name Tarnamid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ Tarnamid® T-30 MS Polyamide 6 - Natural.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High viscosity extrusion grade for blown and flat films, including biaxial oriented films, also for extrusion of rods, pipes, plates, sheets, low diameter tubes and for injection molding of thick-walled parts.For uncolored parts produced by injection molding, contain including and demolding agents.Tarnamid® has the following main properties:High mechanical strength, rigidity and hardnessHigh impact strengthHigh vibration damping capacityGood fatigue strengthVery good sliding properties, abrasion resistance, low coefficient of frictionHigh thermal resistance, admissible temperature of continuous operation from -60°C to +150°CHigh chemical resistance, particularly to organic solvents, oils, lubricants and fuelsConsiderable moisture absorption influencing mechanical and electrical propertiesSelf-extinguishing properties (fire retardant properties)Good electro-insulating propertiesGood optical properties, relatively good transparency of molded pieces with thickness below 3.2 mm made from natural Tarnamid® (not dyed and not compounded)Can be used for the production of goods coming into contact with food (grades fulfilling requirement of European Union Directive No 2002/72/EEC) with latest amendmentsInformation provided by Azoty Tarnow™.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ISO 1183
Water Absorption 1.8 %

@Time 86400 sec
1.8 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
ISO 294-4
Melt Flow 25 g/10 min

@Load 5.00 kg,
Temperature 275 °C
25 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 60.0 MPa

@Load 36.5 kg
8700 psi

@Load 80.5 lb
cond.; ISO 2039-1
140 MPa

@Load 36.5 kg
20300 psi

@Load 80.5 lb
dry; ISO 2039-1
Tensile Strength, Yield 45.0 MPa
6530 psi
cond.; ISO 527
78.0 MPa
11300 psi
dry; ISO 527
Elongation at Break 100 %
100 %
dry; ISO 527
280 %
280 %
cond.; ISO 527
Tensile Modulus 0.980 GPa
142 ksi
cond.; ISO 527
2.80 GPa
406 ksi
dry; ISO 527
Flexural Strength 28.0 MPa
4060 psi
cond.; ISO 178
82.0 MPa
11900 psi
dry; ISO 178
Charpy Impact Unnotched NB
NB
ISO 179 1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
dry; ISO 179 1eA
1.30 J/cm²
6.19 ft-lb/in²
cond.; ISO 179 1eA
Thermal Properties Metric English Comments
Melting Point 221 °C
430 °F
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
cond.; ISO 75
60.0 °C
140 °F
dry; ISO 75
Vicat Softening Point 195 °C

@Load 5.10 kg
383 °F

@Load 11.2 lb
ISO 306
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
Glow Wire Test 750 °C

@Thickness 2.00 mm
1380 °F

@Thickness 0.0787 in
PN-EN-60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
cond.; IEC 93
1.00e+15 ohm-cm
1.00e+15 ohm-cm
dry; IEC 93
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
cond.; IEC 93
1.00e+15 ohm
1.00e+15 ohm
dry; IEC 93
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 243-1
Comparative Tracking Index 600 V
600 V
IEC 112
Processing Properties Metric English Comments
Melt Temperature 230 - 290 °C
446 - 554 °F
Mold Temperature 60.0 - 120 °C
140 - 248 °F
80 - 90°C is recommended
Drying Temperature 75.0 - 100 °C

@Time 7200 - 14400 sec
167 - 212 °F

@Time 2.00 - 4.00 hour
Moisture Content <= 0.10 %
<= 0.10 %
Injection Pressure 80.0 - 130 MPa
11600 - 18900 psi
80 MPa is recommended