Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 8.00 - 165 MPa | 1160 - 23900 psi | Average value: 50.5 MPa Grade Count:86 |
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim.. |
|||
Tensile Strength, Ultimate | 40.0 - 165 MPa @Temperature -40.0 - 150 °C |
5800 - 23900 psi @Temperature -40.0 - 302 °F |
Average value: 70.3 MPa Grade Count:9 |
Overview of materials for Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled". Specific grades with glass content between 15.. |
|||
Tensile Strength, Ultimate | 63.0 - 165 MPa | 9140 - 24000 psi | Average value: 103 MPa Grade Count:31 |
Overview of materials for Polycarbonate/ABS Alloy, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, Carbon Fiber Filled". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Ultimate | 0.0552 - 165 MPa | 8.00 - 23900 psi | Average value: 7.09 MPa Grade Count:1176 |
Overview of materials for Silicone Rubber This property data is a summary of similar materials in the MatWeb database for the category "Silicone Rubber". Each property range of values reported is minimum and maximum values of appropriate Ma.. |
|||
Tensile Strength, Ultimate | 70.0 - 165 MPa @Temperature 60.0 - 150 °C |
10200 - 23900 psi @Temperature 140 - 302 °F |
Average value: 113 MPa Grade Count:1 |
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Tensile Strength, Ultimate | 45.0 - 165 MPa | 6530 - 24000 psi | Average value: 81.1 MPa Grade Count:32 |
Overview of materials for Nylon 66, 30% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are inclu.. |
|||
Tensile Strength, Ultimate | 50.0 - 165 MPa | 7250 - 23900 psi | Average value: 111 MPa Grade Count:83 |
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Ultimate | 114 - 165 MPa | 16500 - 24000 psi | Average value: 137 MPa Grade Count:10 |
Overview of materials for Polyetherimide (PEI), Nickel Coated Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "PEI, NCG Filled". Each property range of values reported is minimum and maximum values of appropriate Ma.. |
|||
Tensile Strength, Ultimate | 3.45 - 165 MPa | 500 - 23900 psi | Average value: 95.5 MPa Grade Count:92 |
Overview of materials for Nylon 6, 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% are included. .. |
|||
Tensile Strength, Ultimate | 70.0 - 165 MPa | 10200 - 24000 psi | Average value: 123 MPa Grade Count:38 |
Overview of materials for Polybutylene Terephthalate (PBT), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Carbon Fiber Filled". Each property range of values reported is minimu.. |